Silver palladium termination * AgPd-terminated capacitors are designed for conductive adhesion. Reflow or wave soldering is not recommended. [EPCOS Multilayer ceramic capacitors, Soldering directions, October 2006] * CONDUCTIVE EPOXY BONDING. Epoxy c
Electronics Forum | Tue Aug 30 09:24:08 EDT 2005 | Slaine
we manufacture a range of ceramic parts that have silver termination,there is already a small leaching problem (absorption of the termination by the solder in liquid form)with Sn62 that we live with, having to implement unleaded solder they are norma
Electronics Forum | Thu Apr 19 16:54:32 EDT 2007 | flipit
I don't suggest using Pd/Ag or Ag/Pd terminated components unless you are forced to use them. You often see a line of demarcation that suggests a poorly wetted solder joint. I have had bad experiences with Pd/Ag terminated capacitors. Even when so
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Tue Oct 23 07:03:52 EDT 2007 | davef
We're not really sure. Usually when solder leaves the pads and wicks-up a component lead, it means the component lead is much warmer than the pad on the board. This is the direction we would have taken this if we hadn't taken the AgPd / conductive e
Electronics Forum | Thu Aug 12 20:32:44 EDT 2004 | usdigital
Indy, We use Palladium silver surface finish parts for silver epoxy attached parts only. It is our understanding that this finish is not for solder, but only silver epoxy attach. I expect that is you problem. Dave
Electronics Forum | Sun Jul 04 19:49:05 EDT 2004 | indy
Hello Everyone, We are having some problem with Palladium-Silver surface finish. We have ceramic components with the above surface finish. When we try to assemble these on Sn/Pb solder, we are observing open joints. If we reflow the compt for more t
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Wed Apr 26 10:27:37 EDT 2006 | slaine
weve hand soldered a few components that were tarnished with no problems, also the tarnish is electrically conductive if it helps.
Electronics Forum | Wed Apr 11 06:56:46 EDT 2001 | brownsj
Most of the component vendors I've dealt with will guarantee the solderability of the terminations for three years if the components are still packaged in a full reel. If the reel is part used we've kept them for 1 year and then used a wetting balanc