Electronics Forum | Fri Dec 16 10:25:37 EST 2005 | solderiron
Rather than cleaning a water soluble flux residue off the board, by encapsulating the product. covering the board or the component with lets say a Hysol encasulant. Would this prevent the active flux residue from migrating and deteriorating the elect
Electronics Forum | Fri Dec 16 11:21:18 EST 2005 | patrickbruneel
Steve, Water-soluble fluxes are per definition very corrosive and need to be cleaned (read the data sheet) Encapsulation will prevent humidity reaching the water-soluble acids but will not prevent reducing the metals the flux is in contact with to m
Electronics Forum | Fri Dec 01 14:12:50 EST 2000 | Jim M.
My company currently uses water soluble paste for our SMT process. We were having trouble retaining hot water in our in line, closed loop DI cleaner. The cleaner kept shutting down when the water temp. dropped below 125C. As a result, the conveyor
Electronics Forum | Fri Jun 01 09:50:01 EDT 2001 | lumidor
Our PCBs manufactured with no clean flux have a waxy film on the board...is this normal? Our contract manufacturer recently switched to no clean from water wash. Thanks Carl
Electronics Forum | Tue Jan 02 14:12:23 EST 2001 | Dave Miller
I work for an R&D company that is starting to do some prototype and limited production circuit cards. We are deciding how we want to build these boards, and we are wondering what we should do about flux and cleaning. We have circuits that run at 15
Electronics Forum | Fri Dec 01 15:37:50 EST 2000 | Dason C
Jim, you may need to look with different paste instead of the cleaning solvent. Please advise what is the paste which you currently using? Beside, when you talking about the board stayed in hot area, is it a drying area or the cleaning zone. If it
Electronics Forum | Fri Dec 01 17:03:57 EST 2000 | Dave F
Curious, very curious ... Residues � Where are these residues? [solder & laminate / mask, solder only, laminate / mask only] What is the result of your analysis to the residues? How do you know it�s a flux residue, rather than a chemical by product
Electronics Forum | Fri Dec 01 16:02:33 EST 2000 | Jim M
Thanks for your reply. I 've tried to clarify and answer your questions. The water soluble paste used is WS3060, type 4. The boards are sent through a inline di cleaner after reflow. There is a hot Di waterwash, rinse and then hot air to dry the wa
Electronics Forum | Fri Sep 15 09:24:54 EDT 2000 | C.K.
At my last place of employment, that was the big reason why nobody (especially the Design Engineers) bought into a no-clean process - interference with high-impedance circuits. One guy was so paranoid about flux residues remaining on the board, that
Electronics Forum | Tue Feb 23 16:45:36 EST 2010 | dyoungquist
Davef is right on as usual. We are doing exactly what you do. Some smt with no clean paste then the plate through connectors on our selective solder machine using water soluble flux. We then clean with a ultrasonic water process. We do see the re