Electronics Forum | Wed Jul 21 17:49:52 EDT 2004 | jsk
problem: Too many solvents and boards are not clean Flux remains on the board after vapor degreaser and "Powdery" white residue after vapor degreasing Flux type is kester 186 Process: hand solder High Temp alloy, spot clean after hand solder e
Electronics Forum | Fri Jul 23 14:41:41 EDT 2004 | Steve Stach
Dear JSK, It sounds like the root causes of your problem are two fold. First, excessive heat will polymerize the abietic acid found in rosin forming neo-abietic diamers and polymers which are much less soluble than the parent monomer. There are
Electronics Forum | Fri Apr 22 05:01:19 EDT 2011 | azrina
Hi, I am doing my master degree in flux cleaning process for flip chip assemblies and required to establish a new receipt for flux cleaning. currently, i am doing screening process for the parameters involve ; temp,pressure, surfactants, speed and a
Electronics Forum | Wed Apr 28 12:08:02 EDT 2010 | tjg
Our latest designs are flip chip on flex based and we have issues with delamination/blistering. We know it is related to our vapor solvent (n-Propyl Bromide based) attacking an inner layer adhesive. Has anyone else ever heard of something like this?
Electronics Forum | Wed Apr 28 14:52:03 EDT 2010 | davef
When we hear the words 'flexible circuit' and 'delamination' in the same sentence, we think: * Excessive reflow temperature. * Entrapped moisture. Boardhouse: I hope this is a step towards redemption.
Electronics Forum | Mon Mar 25 21:45:22 EDT 2024 | buckeye
I got an inquiry from one of our electronics labs with regards to their soldering processes. They use eutectic (63% Sn, 37% Pb) solder. For liquid flux they are currently using Kester 186, which is an old-school, full rosin (RMA and ROL1) flux that c
Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi
we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Fri Jul 23 09:14:28 EDT 2004 | davef
Consider your flux suppliers recommendations when determining the proper cleaning method for your boards.
Electronics Forum | Mon Jul 26 16:31:02 EDT 2004 | Sue PH
We use Kester 186 flux and the STU people would sometimes find white residue after cleaning with Isopropyl at the solder station. We have Lenium (Petroferm)in our vapor degreasers, and now they use Lenium at their stations as well as final clean, an