Electronics Forum | Fri Jun 01 10:52:37 EDT 2012 | blnorman
Neither the Omega meter nor the IC are officially "destructive" tests, but everywhere I worked we treated them that way. The boards were scrapped after the test. The Omega meter can be tested at elevated temps, but the IC sample is extracted at ele
Electronics Forum | Wed Feb 16 21:51:29 EST 2000 | Dave F
Kurt: Lots of choices, not many of them good, yano. 1 So LPI has taken over the market pretty nearly 100%, but it won't "tent" reliably, because it is not very viscous when applied and drops into the hole. So then, tenting/plugging with LPI is bad
Electronics Forum | Wed Feb 16 21:51:29 EST 2000 | Dave F
Kurt: Lots of choices, not many of them good, yano. 1 So LPI has taken over the market pretty nearly 100%, but it won't "tent" reliably, because it is not very viscous when applied and drops into the hole. So then, tenting/plugging with LPI is bad
Electronics Forum | Sat Oct 06 08:32:09 EDT 2001 | davef
Mr. Wizard is not currently available. You get the wizzer. Maybe your dream date will show later. Get your own lab tests done. Show your potential customer that your boards are clean. That�s the issue. The issue is not how you go about cleaning
Electronics Forum | Thu May 09 17:13:10 EDT 2002 | davef
We are converting all our ENIG to imm silver. CHARACTERISTICS * Nominal thickness of the deposit will be 0.1 to 0.3 microns. * Deposit is flat and uniform * It will withstand multiple heat cycles in assembly, which can be problematic with tradition
Electronics Forum | Mon Apr 06 12:32:20 EDT 1998 | Roxanne Picou
March 31, 1998-Austin, TX --- Austin American Technology announces a new Pre-Wash feature for the Mega� II to operate in conjunction with AAT's patented closed-loop regenerative cleaning process. This feature allows for an optional dual chemistry
Electronics Forum | Mon Oct 16 20:29:32 EDT 2000 | Dave F
Jason: How did you determine that the deposits are tin oxide? What does this stuff look like? Klein Wassink "Soldering in Electronics" (p. 221, quoting original work by others). States (in effect) tin (or solder) quickly forms a protective oxide
Electronics Forum | Fri Jan 11 17:14:13 EST 2002 | davef
We have one product with electroless nickel, immersion silver solderability protection. We do not purport to be experts, but like many things, have seemingly boundless opinions. Side note: There are a least three different [maybe five] imm silver
Electronics Forum | Wed Sep 22 02:45:23 EDT 1999 | Brian
| | Dear All, | | | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | | | I mean that I wonder
Electronics Forum | Sun Nov 08 15:27:25 EST 2015 | davef
Thinner: Flux thinner, NOT paint thinner We kept a spare stone in thinner in inventory. We cut PVC pipe to size, cap in one end, screw thread on the other, stone inside, filled with flux thinner and covered with a screw cap. I don't remember who we