Electronics Forum | Sun Aug 10 03:41:20 EDT 2008 | eyalg
Thanks for your promt reply It was very usefull Eyal
Electronics Forum | Sun Aug 10 03:39:21 EDT 2008 | eyalg
Thanks Pete yes we usu ROHS solder paste in our process. I agree that this termination is more suitable for adhsive bonding rather than soldering. We'll try changing the termination type as you recommended. Eyal G
Electronics Forum | Fri Aug 08 09:49:17 EDT 2008 | scottp
We've seen the exact same problem. The solder joints had negative wetting angles and x-sections show that the PdAg termination dissolved into the solder. We no longer allow PdAg terminations.
Electronics Forum | Thu Aug 07 10:02:10 EDT 2008 | eyalg
We are facing low quality due to soldering opens with coilcraft inductors 0402CS-2N7XGLW. The termination used is(suffix L =RoHS compliant silver-palladium-platinum-glass frit. Did anyone had this problem in the past? Can we do better using T = RoH
Electronics Forum | Thu Aug 07 11:58:36 EDT 2008 | pbarton
We have experienced the same problem with Pd/AG and P/Ag terminations on precision resistive parts. The problem is dissolution of the termination metallisation into the bulk solder. This is exacerbated by the higher thermal profiles required for RoHS
Electronics Forum | Mon Feb 20 08:25:13 EST 2006 | Rob
No problem. If you get no joy you're going to have to change the footprint to a 1206 or 1210. Murata have a range of high Q value inductors (50-60) & from memory Toko used to be pretty hot too. The terminations on the coilcraft part are listed a
Electronics Forum | Thu Feb 16 12:07:19 EST 2006 | dpmilk
We have been using Coilcraft 1008CS inductors for several years. We have had problems with them turning green when we use lead-free solder paste. We have tried several solder pastes (water soluble and no-clean)from different manufacturers, but the
Electronics Forum | Sat Feb 06 16:28:09 EST 2010 | mystkldy
I have some large ROHS SMT inductors that are moving during the reflow process. I have tried adding extra solder, gluing and doing both. I don't know what else to try, any suggestions?
Electronics Forum | Wed Aug 27 23:00:55 EDT 2008 | omid_juve
i mean that the parts that we have here is ROHS compliant(pb free)but the process that we have(the type of solder paste & the surface finish of the board has pb in its mixture) this is not the cause of problem ?
Electronics Forum | Fri May 27 08:11:27 EDT 2005 | Joris Groot Koerkamp
I have a problem with a Murata cap chip type resonator(ROHS). After the reflow process, the soldering joints flow to one side of the component. I did not have this problem with the leaded component. Did someone have a solution for this problem?