Electronics Forum | Wed Sep 15 11:44:46 EDT 2004 | mriddle
Dear SC, Are you looking for a cold solder detection tool for SMT,through-hole or both?
Electronics Forum | Tue Sep 14 06:00:27 EDT 2004 | sc
dear, appreciate the sharing of experience on detection tools of cold soldering defect on PCBA. thanks SC
Electronics Forum | Tue Sep 14 06:00:31 EDT 2004 | sc
dear, appreciate the sharing of experience on detection tools of cold soldering defect on PCBA. thanks SC
Electronics Forum | Fri Sep 03 11:45:15 EDT 2004 | rlackey
Hi Ken, I know this doesn't help in the immediate timescale, but isn't avoidance the best form? can you trace the cracking to a process issue (Solder profile, shock damage, handling damage, probe/ATE damage)or a chip cap manufacturing fault? I can'
Electronics Forum | Thu Apr 28 17:02:07 EDT 2011 | grasso1976
Has anyone had success utilizing the lifted lead/ height checker feature on a Mirtec MV-7L. We recently had two separate events where the machine did not detect a lifted lead using the ic/bridge inspector. The soldering results came back with out def
Electronics Forum | Wed Jan 07 07:16:25 EST 2004 | davef
Cold solder prior to properly performing a well designed drop test. Actually, "cold solder" means different things to different people. Two dull solder connection conditions are: * "Disturbed" solder joint: a solder joint that has an "angular face
Electronics Forum | Tue Jan 06 19:53:32 EST 2004 | jj
Hi, Any idea what's the possible causes of cold solder after drop test? Thanks JJ
Electronics Forum | Thu Aug 12 21:06:48 EDT 2010 | ptpaazmi
COLD SOLDER LOCATION U600/U601 Problem : Several XMp3i Rotary swithes were found to exibit intermittent function during a DV build at WNC
Electronics Forum | Tue Aug 24 20:15:27 EDT 2010 | davef
What is ... and how does it pertain? * Location U600/U601 * XMp3i Rotary swithes * DV build * WNC
Electronics Forum | Sun Jan 18 10:13:59 EST 2004 | davef
Materials added to solder can change its appearance. For instance: * Gold in tin/lead solder is dull / grainy * Palladium in tin/lead solder is dull / grainy We do NOT advocate using visual appearance to define the appearance of a good and a bad so