Electronics Forum | Wed May 08 04:46:25 EDT 2013 | mbb
Hello, I want to ask what are causes that could engender rejected components in Panasonic pick and place machine?
Electronics Forum | Thu Jan 14 23:49:00 EST 1999 | Wirat Sriamonkitkul
I saw the problem of void in solder bump or in lead less component or some BGA. But I didn't have standard specification of that void is accept or reject? Do any body have the better idea or suggestion of the criteria ? Thank you, Wirat S. / Jan 15
Electronics Forum | Sat Jul 22 13:20:35 EDT 2023 | shrikant_borkar
Dear Abhishek, I too got the opportunity to investigate this defect Lift lead for SOT. Lead lift in IC, and SOT can occur due to various reasons. Here are some possible reasons for lead lift and ways to avoid them: During the assembly process, mecha
Electronics Forum | Fri Jan 15 08:11:34 EST 1999 | Jim Nunns
Our spec on voids is 30% ball diameter in the center. On the component to ball and pad to ball interface, we use 25%. To determine this spec, we asked around. I don't know of any studies that have been done to verify if this is OK Regards Jim |
Electronics Forum | Fri Jan 15 08:09:56 EST 1999 | Jason Hall
| I saw the problem of void in solder bump or in lead less component or some BGA. But I didn't have standard specification of that void is accept or reject? Do any body have the better idea or suggestion of the criteria ? | | Thank you, | Wirat
Electronics Forum | Thu Feb 19 12:52:08 EST 1998 | Earl Moon
| what is your experience about the presence of the voids in the joints ? | Are they dangerous and when ? My specifications require rejection and study if voiding exceeds 2% of solder joint volume measured using x-ray and/or x-sectional analysis. My
Electronics Forum | Fri Dec 27 12:47:21 EST 2019 | ameenullakhan
Dear Team, We are facing open solder issue in a sensor component. Rejection rate is 2 out of 50 components placed. The issue is very random. We have tried increasing the solder paste height from 5 mil to 7 mil. The issue persist still. Differen
Electronics Forum | Fri Jan 15 15:29:03 EST 1999 | Jason Hall
| Our spec on voids is 30% ball diameter in the center. On the component to ball and pad to ball interface, we use 25%. To determine this spec, we asked around. I don't know of any studies that have been done to verify if this is OK | | Regards | Ji
Electronics Forum | Fri Jan 15 09:27:18 EST 1999 | Earl Moon
| I saw the problem of void in solder bump or in lead less component or some BGA. But I didn't have standard specification of that void is accept or reject? Do any body have the better idea or suggestion of the criteria ? | | Thank you, | Wirat
Electronics Forum | Fri Jan 15 13:35:03 EST 1999 | Terry Burnette
| I saw the problem of void in solder bump or in lead less component or some BGA. But I didn't have standard specification of that void is accept or reject? Do any body have the better idea or suggestion of the criteria ? | | Thank you, | Wirat