Electronics Forum | Sun Jun 30 20:00:56 EDT 2002 | redmary
the SOIC encounter solder crack after reliability test, the common process is: SMT---manual soldering---IPT(in process test)---potting---T/C(thermal cycling,only add current and voltage)---B/T and F/T (burn in and functional test). the condition is 2
Electronics Forum | Mon Jul 01 15:37:56 EDT 2002 | pjc
Possible cause can be design related- if the solder land is too small. Check w/ IPC SM-782 Solder Land Design Guide Another is board finish. I have seen problems like this with Gold finished PWBs- which creates a more brittle solder joint.Another pos
Electronics Forum | Mon Jul 01 20:42:54 EDT 2002 | davef
Comments [questions] are: * It�s strange that an uggie ol� SOIC, 50 pitch, BIG honkin� solder pad, kinda thang is failing. Sumpin aint kosher, yano? * Where is the failure occurring [ie, lead to pad, pad to board, etc]? Talk about the breadth and di
Electronics Forum | Wed Feb 20 23:17:34 EST 2002 | surachai
I AM JUST EVALUATION LEAD FREE EVALUATION AND FOUND THE BIG PROBLEM OF SOLDER CRACK BETWEEN TERMINAL OF COMPONENT AND THE INTERMETALLIC LAYER OF LEAD FREE ALLOY BUT DON'T FIND ANY CRACK BETWEEN SOLDER AND SURFACE OF PCB , COULD YOU HELP ME VERIFY T
Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Wed Sep 27 12:44:52 EDT 2000 | Ashok Dhawan
What could be possible resons for " Plating Crack on Barrel (tented via)" This tented via is in proximity to parts being hand soldered. The crack in barrel was detected on failure analysis - micro-section of via where barrel is having crack ( circul
Electronics Forum | Tue May 25 07:03:34 EDT 1999 | Milan Z.
After reflow proces in convection-IR oven we find broken body of SOT23 elements. There is no problems on other elements (SOIC, chip R,chip C, etc) Where is the problem? Thanks in advance!
Electronics Forum | Fri May 31 10:15:30 EDT 2019 | davef
Major sources of crack in the solder connection after thermal cycling are: * Thermal heating caused by differences in thermal expansion between the board and the component * Lead-free solder is more rigid and brittle than eutectic solder in simila
Electronics Forum | Mon May 10 11:24:33 EDT 2004 | Charly
Encounter solder ball crack after reflow, found the solder ball is out of shape after reflow, cross section view found that the solder mask opening is not good ( when we do comparason with diff. supplier substrate.) Does the solder mask shape will af
Electronics Forum | Mon Jun 24 23:21:27 EDT 2019 | sssamw
You may need tell us the background, how PCBA being tested, the test setting and spec. Solder crack maybe due to CTE mismatch or mechanical strain.