Electronics Forum | Tue Aug 17 11:28:07 EDT 2004 | rlackey
Hi, I'm not the expert DaveF is, however I have seen quite a few cracked chip capaictors in my time - most of these were from lack of Z height adjustment on a turret chipshooter to compensate for various thickness. Do you have separate 1206 thick
Electronics Forum | Tue Feb 28 16:09:27 EST 2006 | outgasser
Does anyone have any insight as to the cause of cracked chip capacitors during SMT? Z-stop? Thermal shock? Any help is appreciated.
Electronics Forum | Tue Feb 28 16:53:26 EST 2006 | slthomas
Depaneling with the parts in question near a V-score?
Electronics Forum | Tue Feb 28 17:08:09 EST 2006 | outgasser
Steve, I believe you hit it right on the head! Thanks! Gary
Electronics Forum | Thu Mar 02 13:20:26 EST 2006 | inds
jagman, take a hard look at a capacitor under the high mag microscope before you start assembling it.. I remembering seeing cracks even before the assembly. apparently all chip capacitors have crack at the intersection between the capacitor head and
Electronics Forum | Wed Mar 01 12:28:48 EST 2006 | Chunks
Round cracks that look like it's from a placement are generally from a too big Delta T in wave (been there done that). All other cracks are anomalies. Ya gotta see it find it.
Electronics Forum | Tue Feb 28 17:09:40 EST 2006 | outgasser
PWH, Thanks for all your input. All these areas are of concern which I will look closer into. thanks! gary
Electronics Forum | Tue Feb 28 16:58:39 EST 2006 | PWH
Too fast heating/cooling rate in reflow (look at mfg's spec.). Z "overdrive" on pick and place or chipshooter though unlikely I would say. Depanelization method (bending a scored board to break it is tough on things). Bad PCB design - cap. too clo
Electronics Forum | Thu Sep 11 15:23:31 EDT 2003 | Peter L.
I have come across a rash of failed assemblies that have 0805 capacitors and resistors, bottom side glued, wave soldered and washed. Trouble shooter reported touching up the solder joints on a few areas and the boards would pass test. I had a look a
Electronics Forum | Wed Aug 18 08:58:49 EDT 2004 | M.Enright
We are finding cracked capacitors at both first pass and second pass.