Electronics Forum | Tue Jun 06 11:57:12 EDT 2006 | Chunks
IPC 610 says acceptable Class 1 (Class 2, 3 indicator) if they are entrapped/encpsulated balls within 0.13mm of lands or pads. or exceed 0.13mm in diameter. Defect Class 1,2,3: Solder ball violates min electrical clearance. Solder balls not entrap
Electronics Forum | Tue Dec 02 07:56:40 EST 2008 | realchunks
Wow, rocket science with Nasa specs! I like it. I don't see the trick question here, so I'll continue.... IPC simply states over hang of round or flattened (coined) leads is acceptable (class 1, 2, & 3) if it "does not violate minimum electrical c
Electronics Forum | Fri Aug 26 17:27:48 EDT 2005 | saragorcos
Hello there, Most probably, since the solder balls are entrapped, it is a process indicator, but refer to IPC 610-6.5.3.1 on Excess solder / solder balls / splashes - it really depends on what class you are manufacturing, and the minimum electrical c
Electronics Forum | Thu Jan 31 13:01:33 EST 2013 | kmots15
Defect if its not coated. Defect - Class 1,2,3 • Solder balls are not entrapped, encapsulated or attached or can become dislodged in the normal service environment. • Solder balls violate minimum electrical clearance.
Electronics Forum | Wed Jan 01 22:19:33 EST 2020 | sssamw
Solder ball attached on solder joint without violation minimum electrical clearance is acceptable. If your process parameter including stencil not changed, suggest you check if solder pasted being pushed out after IC placement, also check if solder j
Electronics Forum | Mon Jul 16 15:49:33 EDT 2001 | Steve
The solder balls you are talking about are caused by too much paste. Reduce the size of the stencil aperatures. Concerning removing the solder balls, the first thing you need to ask yourself is, do I need to remove them. IPC-610, 12.4.10 states, "Ac
Electronics Forum | Thu Nov 29 17:30:07 EST 2001 | davef
You give no clue of what you want to write about. Let's try this: J-STD-001, 8.3.1 Particulate Matter says words to the effect of solder balls / splats shall be neither: * Loose or able to be dislodged during normal service � NOR * Violate minimu
Electronics Forum | Mon Jun 11 22:00:19 EDT 2001 | davef
IPC-A-610 uses words to the effect that it�s a Class 2 process indicator, if either: * Entrapped or encapsulated solder balls that are within 0.13 mm [0.00512 in] of lands or connectors, OR * Entrapped or encapsulated solder balls exceed 0.13mm [0.00
Electronics Forum | Tue Nov 19 21:38:39 EST 2019 | zack
Hello, The first thing that you need to do is to make process mapping about this incident, so you can exactly determine all factors and observable changes happened during 2 weeks of timeline difference. According to my experience, if all equipment
Electronics Forum | Mon Aug 28 12:41:35 EDT 2000 | JAX
MoonMan, I'll take a crack at the list. Feel free to answer the ones I don't! 1. Solderability is a parameter which indicates how well a component can be soldered. As far as Solder Termination Coatings go, here are some up�s and down�s of a few. Ha