Electronics Forum: eni (Page 1 of 3)

problem in solderability

Electronics Forum | Wed Sep 10 12:44:55 EDT 2008 | vladig

Well, it wasn't as easy to figure out the root cause. The last image is below. It shows how the board finish looks like (the trace was under solder mask). AS you can see, the layer of E-Ni is spliting (the board shop admitted the problem afterwards).

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 12:37:05 EST 2008 | realchunks

Long, yellow, ugly toe nails will have the same affect on your boards.

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 15:08:35 EST 2008 | srmlan

I guess you are right, they both need some loven

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 15:36:22 EST 2008 | mumtaz

Oh my, a Ford? Did you lose a bet?

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 14:34:16 EST 2008 | srmlan

I have not had problems with ENiG panels, but they were made state side. We had Trace Labs cross-section them and found no problems. Whats this about yellow nails? Mine are full of grease from constantly having to fix the Jeep. I would try to pop my

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 10:43:49 EST 2008 | samir

Folks, what is the industry consensus? Which is the more popular lead-free, flat finish these days? Here's what I know from my experience. IAg: 1. Quality of finish is dependent on supplier 2. Can NOT be reworked. It is known that reworking t

Black Pad?? (PICTURES)

Electronics Forum | Mon Oct 20 15:14:59 EDT 2008 | robinj

Yup, just read that in the link Patrick sent. > Thanks again... Im going to have everyone screen > the boards for this carefully before processing. > I have also sent the board manufacturer an email > to get their comment on the matter. No PCB ve

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 12:10:38 EST 2008 | samir

Thanks, I stand corrected on the tarnish definition. Thanks for the input too. That's exactly what I wanted.

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 13:12:55 EST 2008 | shrek

KRIKIES Chunks me-lady. Yellow toe-nails with tree rosin will definitely sodder that there immersion silver. Sounds like i have met me match. Who is this fella with the toe-nails?

ENiG or IAg? Which is better?

Electronics Forum | Thu Mar 06 14:06:50 EST 2008 | realchunks

Some guy who things he's cool cause he drives a Vette whilst his collar is up.

  1 2 3 Next

eni searches for Companies, Equipment, Machines, Suppliers & Information

SMTAI 2024 - SMTA International

Reflow Soldering 101 Training Course
Electronics Equipment Consignment

High Precision Fluid Dispensers
Electronic Solutions R3

Low-cost, self-paced, online training on electronics manufacturing fundamentals