Electronics Forum | Mon Aug 16 11:49:44 EDT 2004 | Kris
Hi Guys thanks for the replies. Dave, the spec is not for enig but for hard gold does your response alter if thats the case /
Electronics Forum | Mon Aug 16 16:26:19 EDT 2004 | Kris
what about areas that are soldered ? This is def not a Enig process and the specs are as they are not sure why thanks a lot for your help
Electronics Forum | Mon Aug 16 13:18:46 EDT 2004 | davef
You bet our reponse changes. Q2R: Hard gold thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2R: This is a hard gold spec?? It looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. The gol
Electronics Forum | Mon Aug 16 16:37:08 EDT 2004 | davef
As we mentioned in an earlier response in this thread [Q5], you do NOT want to solder to hard gold. Hard gold is a wear surface. [That's IT, that's the LIST.] If you want to solder to gold, then either use: * IPC-4552 ENIG specification, mentioned
Electronics Forum | Wed Aug 11 18:36:03 EDT 2004 | davef
90 Knoop. Q2: Thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2: This looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. [IPC-4552 ENIG specification: * Gold thickness of 0.075 - 0.125
Electronics Forum | Fri Mar 24 18:07:25 EST 2006 | Chris
Flash gold is just thin gold plating over electroless nickel or electrolytic nickel. Flash gold is electrolytic gold where the panel is connected to a plating rectifier and current causes the plating process to occur. Gold thickness is controlled b
Electronics Forum | Fri Mar 24 15:44:11 EST 2006 | Hoss
I have no experience with soldering to a flash gold finish. We have specified ENIG for a prototype PCB order and the supplier is asking us if they can use flash gold. They are telling us that the two are interchangable which I don't believe. The
Electronics Forum | Sat Mar 25 07:10:12 EST 2006 | davef
We agree with Chris. If your gold is applied properly and is the correct thickness, you will see no difference. One nit on Chris' comments: immersion gold will plate-out [self-limit] around 8 thou, although we've heard 12 thou.
Electronics Forum | Thu Apr 20 05:57:55 EDT 2006 | Huub
Do you have experience with wear resistance of spring contacts on ENIG vs Flash Au? regards, Huub.
Electronics Forum | Mon May 11 11:05:08 EDT 2009 | milas
Hi 1. Does anyone know what the pros and cons are of ENIG vs Electroplating ? 2. Is there a likelyhood that in either of these processes the gold can flake off after a period of time ? Thanks in advance Milas