Electronics Forum | Thu Sep 02 16:12:51 EDT 2004 | Mike Konrad
Hi -K We are a manufacturer of ionic contamination testers (not yours). In most cases, automatic mode is appropriate. In some instances however, you may need extra time to �release� entrapped contamination from the sample. Automatic mode is not a
Electronics Forum | Fri Jan 21 16:50:33 EST 2005 | Board House
I work for a board house and our proceedure for this process is the following, We cover the via pads leaving the hole open and then apply the surface finish and then go back and Cover the Via with a second operation. By doing this you do not entrap
Electronics Forum | Sat Jun 01 04:27:37 EDT 2019 | gregoryyork
Increase paste volume and use ramp soak spike profiling. Reducing volume of paste often leads to entrapment. Good idea to know difference between voiding and dewetting due to contamination
Electronics Forum | Fri Jan 03 19:17:12 EST 2003 | Mike Konrad
Hi Richard My experience with R.O.S.E. testers has been positive with regard to detecting ionic contamination (even exceptionally low levels). As previously mentioned, a good R.O.S.E tester will be able to detect minuet levels of ionic contaminatio
Electronics Forum | Fri May 21 14:22:56 EDT 1999 | Dave F
| Dave, | i tried reflowing bare boards with only solder printed on em and no component placed. we still got voids as same as when components were placed. so atleast one of that theories(voids due to component/component placement)could be considered
Electronics Forum | Mon Jun 04 09:15:08 EDT 2012 | davef
bwjm: Delamination can be attributed to several factors: * Entrapped moisture, processing solutions, and what not that expands when heated to normal soldering temperature * Excessive soldering temperature * Excessive laminating temperature * Def
Electronics Forum | Thu Mar 23 08:34:45 EST 2000 | Shane Lay
Dave, Thank you for the information. We will be conducting several tests in the near future that will evaluate the corrosion/contamination response as it is our primary concern once we remove our aqueous processes. We are well aware of the effects
Electronics Forum | Thu Dec 05 11:36:30 EST 2002 | William Guatemala
Have you check the flux gravity lately? If not, Check the flux gravity every 6 hours to make sure proper parameters are meet. Here is a list of things that may cause your solder ball problems; Excecive heat, defective fixtures, preheating temperature
Electronics Forum | Tue Mar 16 18:27:34 EST 1999 | Earl Moon
| We are having a small number (~2%) of our boards pass our manufacturing diagnostics, fail once they reach the customer, fail when they get back to us and then start working again after handling them for a short time. We have eliminated a lot of it
Electronics Forum | Sat Feb 14 19:35:51 EST 1998 | C. Lao
Mr Lao We have some specialist knowledge on this subject and offer both equipment and services for these tests. My first recommendation is that take coupons manufactured by your PC Fabricator and then samples at each manufacturing stage: Bare coupon