Electronics Forum | Mon Nov 05 00:51:58 EST 2007 | omidjuve
We have a problem with soldering of a 96 pin header connector(9001-11961c00l1a from kingmate) we use 3 different wave soldering but in all of the machines we have many short circuit between the pins . the wave soldering machines that we use is fr
Electronics Forum | Fri Dec 27 02:11:31 EST 2019 | anteiv
Hello, We are having problems with SMD wave soldering (ERSA) used flux is BALVER ZINN 390-RX-HT https://www.balverzinn.com/tl_files/balverzinn/downloads/intern/TDB/PDS_390-RX-HT_EN.pdf https://www.balverzinn.com/tl_files/balverzinn/downloads/datenb
Electronics Forum | Thu Dec 29 09:20:30 EST 2005 | Cmiller
We have tested SN100C and SAC305 in our selective solder machine (Ersa Versaflow). We wanted to test both alloys in the selective first because the investment in filling the pots is minimal. In our initial tests the SN100C alloy appears to be the bes
Electronics Forum | Mon Jan 14 02:22:51 EST 2008 | ilona
David, why not contact the current suppliers of selective soldering systems for a copy of their layout specs? Surely we all would be interested to provide potential customers with the info they need to evaluate a process applicabilty or to design bo
Electronics Forum | Thu Apr 20 02:17:15 EDT 2017 | cromaclear
Hello to all, I am having a serious problem on my ersa versaflow 3 machine. This is a selective soldering machine and a problem is in less soldering material on the pins, you can see it in the picture http://imgur.com/a/FC2a1 Do you have any idea how
Electronics Forum | Sat Sep 11 10:51:59 EDT 1999 | JohnW
Folk's, Been asked / told by my boss to look into our board prepping area for wave soldering and find another way of doing it. Thing's I'm looking at are: PCB Breakout - do you do it before or after wave Connector's that need to be pressed in due to
Electronics Forum | Fri May 12 11:40:25 EDT 2006 | solderiron
If you can change to SN100C do it. The nickel prevents the high tin content from eating away at the metals on the tips. Similar to what the Lead did in 63/37 alloys. This Koki crap is just that, crap. 99% tin??? Thats what is causing the problem peop
Electronics Forum | Fri May 12 07:53:40 EDT 2006 | egrice1
Sheldon, Tip life is directly related to temperature, IRON plating thickness on the tip, Alloy composition used and operator technique. High tin contents in lead free alloys attach the tips. Poor wetting and higher melting temperatures cause us
Electronics Forum | Thu Sep 01 14:24:44 EDT 2005 | lsmith
I do not have a ERSA Versaflow but do have some ERSA equipment. Only can tell you I will most likely not purchase anything else from them. The experience I have with their service after the sale would have to be rated VERY low. In addition, they emai
Electronics Forum | Tue Sep 06 15:54:20 EDT 2005 | SC
tried the Pillarhouse??