Electronics Forum | Wed Jun 17 16:08:37 EDT 1998 | upinder singh
We are facing a problem of high contamination on boards after wave soldering. We want the contamination to be under 24 ugm/inch square. We are using a no clean flux with the spray fluxer unit of wave soldering. The contamination is higher on the end
Electronics Forum | Wed Jun 17 16:19:10 EDT 1998 | Ryan Jennens
| We are facing a problem of high contamination on boards after wave soldering. We want the contamination to be under 24 ugm/inch square. We are using a no clean flux with the spray fluxer unit of wave soldering. The contamination is higher on the e
Electronics Forum | Thu Apr 16 13:40:08 EDT 1998 | Chrys
| Is there anybody to help me ? | We have small balls appearing on the boards soldered by | wave soldering machine and it looks that use of nitrogen | is linked to the problem (because without nitrogen, we have no more | problems). | That remind you
Electronics Forum | Tue Mar 10 04:40:01 EDT 2015 | vb7007
Hi I have been struggling with boards for high quality picky customer. I am getting flux waves (like splashed - too hard to clean) after wave, where as we are still using Kester 979 (No clean flux, but as we are getting visible marks which looks si
Electronics Forum | Sat Sep 12 09:49:38 EDT 2015 | davef
If the boards were still "wet" after DI wash, your [I assume] low res flux could be reacting with the moisture on the board and causing the white spots. The preheater in the wave could have more dryification than the preheater on the selective solde
Electronics Forum | Fri Sep 11 15:27:50 EDT 2015 | u4bga
Hi! We're noticing white spots on 2 PCBAs after the selective soldering & DI Wash processes. ----Facts---- 1) The marking is on all boards, irrespective of date code 2) It only happens on leads that have been selective soldered 3) The pattern of w
Electronics Forum | Fri Mar 19 11:01:42 EST 1999 | Dave F
| Hi folks, | | I am looking for inputs on a long-standing problem encountered in our shop: Bottom-side parts (passives) falling off in the Wave...where the only remnants of the part is a flattened glue dot of proper diameter and volume, and somet
Electronics Forum | Thu Jun 14 15:29:29 EDT 2012 | davef
That you can get good solder flow when hand soldering seems to indicate that the temperature of your solder pot is too low. Still, I'm uneasy that you see gold on the pads after passing the board across the solder pot. Gold is so thin with ENIG. So
Electronics Forum | Tue Mar 10 04:36:41 EDT 2015 | vb7007
Hi I have been struggling with boards for high quality picky customer. I am getting flux waves (like splashed - too hard to clean) after wave, where as we are still using Kester 979 (No clean flux, but as we are getting visible marks which looks si
Electronics Forum | Tue Mar 10 04:37:32 EDT 2015 | vb7007
Hi I have been struggling with boards for high quality picky customer. I am getting flux waves (like splashed - too hard to clean) after wave, where as we are still using Kester 979 (No clean flux, but as we are getting visible marks which looks si