Electronics Forum | Tue Feb 07 11:55:27 EST 2023 | tommy_magyar
What I would look at is the chemicals being used in the facility where the complaints are. Flux/flux gel, IPA, cleaning agents, etc. Perhaps you should limit the usage to certain people only, who would be trained how to properly use these. Something
Electronics Forum | Thu Mar 10 13:05:41 EST 2005 | patrickbruneel
This phenomenon is caused by a high amount of halogens (Cl, Br etc.) used in the flux activators or in the flux surfactants. We've seen effects creating all colors of the rainbow. Changing to No-Clean (halide-free) will eliminate this color effect.
Electronics Forum | Thu Mar 10 10:06:08 EST 2005 | steve
OK all you Gurus here's one for ya. Customer is tinning wires with standard eutectic solder in a solder pot. There is a blue tint to the solder in the pot. After tinning with OA flux, which I will change to NC shortly, he has clear teflon insulation
Electronics Forum | Thu Mar 10 15:43:06 EST 2005 | steve
Thank you both for your assistance. I knew that I could count on you folks. The customer has purchased No-Clean flux and is using it as we speak. Hows that for customer service.... All in a days work... Thanks again You make me look good!!! Steve
Electronics Forum | Sat Oct 01 11:48:45 EDT 2005 | Hiram
Hello everybody, We are in the process of implementing NC process on the wave solder. We have a Sonotek XL fluxing system. Any ideas out there? Solder used: SN100C Flux options so far: 264-5 flux, 270WR VOC-free 9both from AIM solder) The flux ch
Electronics Forum | Fri Sep 04 02:09:03 EDT 2009 | sachu_70
Hi Walter, Do you refer to a sprayfluxer operation? The problem seems to be a parameter setting issue. 1. Ensure the wide angle spray reaches PCB with optimum jet pressure. You could pass a glass plate to understand flux coverage and view Jet pressur
Electronics Forum | Wed Apr 26 10:21:09 EDT 2006 | slaine
Hi you need to dip long enough for the temperature of the part being soldered to reach about 20 degrees above liquidus of the solder. For the small parts we dip solder we had Sn62 and SAC387 baths set to 250 degrees and this seems to work best for us
Electronics Forum | Fri Apr 05 10:34:46 EDT 2013 | mandm
Hey Hi, I am new engineer in Electronic Manufacturing Industry. I have a similar problem here,operator applies the flux by dipping the PCB in the flux bath. So could anyone please help me with following questions 1) What could be the possible impacts
Electronics Forum | Fri Jun 26 00:33:08 EDT 2020 | victorzubashev
Hello everyone, Can you please recommend a sensor to measure (contactless) level of solder inside of the wave soldering bath? ideally it should be a sensor that can reliably measure distanceto the melted solder and provide distance (as a codified si
Electronics Forum | Thu May 07 08:12:06 EDT 2009 | milroy
Hi I recommend you to check the exhaust sensor, the ERSA EWS500F is sensing the exhaust before it activates the fluxer. If the exhaust is not working then machine does not start to avoid the sprayed flux emit to the work environment. There is a sens
Industrial Sensor Vision International specializes in advanced camera technology of high resolution fast speed cameras for automation, AOI, 2-D/3-D, SPI inspection and wafer inspection.
3 Morse Road 2A
Oxford, CT USA
Phone: +1 203 592 8723
winsouce.jpg)