Electronics Forum | Sun Sep 27 23:10:19 EDT 2009 | hallwayit
Hi, Walter, Why don't you try no-clean flux? We ever met the same condition, later, we changed to no-clean flux solved the problem.
Electronics Forum | Thu Sep 03 11:20:41 EDT 2009 | thunderdog5000
I have a customer that is having a flux residue problem after wave soldering. Flux is roaring through the board to the top side and leaving a residue. This is only happening on the flat stamped leads. The round leads are fine. They are using Supe
Electronics Forum | Fri Sep 04 02:09:03 EDT 2009 | sachu_70
Hi Walter, Do you refer to a sprayfluxer operation? The problem seems to be a parameter setting issue. 1. Ensure the wide angle spray reaches PCB with optimum jet pressure. You could pass a glass plate to understand flux coverage and view Jet pressur
Electronics Forum | Thu Aug 20 14:52:40 EDT 2009 | davef
Armando: We're guessing that the white residue is on the laminate also. We believe that the residue has something to do with your low residue flux and water. It could be: * Water contamination in the flux. * Poor selection of preheat temperature that
Electronics Forum | Thu Jan 18 15:28:10 EST 2007 | CK the Flip
If you are, in fact, running a No-Clean solder paste: Different no-clean solder pastes will leave different types of (benign) residues. If your paste has been qualified from a Bellcore/SIR/Electromigration standpoint, any residues remaining will NO
Electronics Forum | Thu Aug 20 08:24:07 EDT 2009 | padawanlinuxero
Hi ! In both solder mask and solder joint, I am going to upload a picture today promise, I use only IPA and a ESD brush this kinda clean the problem
Electronics Forum | Thu Aug 20 00:16:56 EDT 2009 | padawanlinuxero
Hello I am having a problem with the flux in the wave solder, I am using a sonoflux 9000 this machine uses a air knife to spray the flux, it creates a mist that when hits the air knife pulls the mist up to the pallet where the board is, but for som
Electronics Forum | Mon Mar 29 04:00:01 EST 1999 | Vinesh Gandhi
Glenn, i am aware of one unique problem with voc free fluxes. since these fluxes have certain amountb of water content they cause sputtering leading to solder balls & voids problems. Regards Vinesh Gandhi | I require some feed back from any one
Electronics Forum | Thu Jan 20 10:12:08 EST 2005 | patrickbruneel
Mike, I totally understand your position. We find ourselves in two opposite camps. If no-residue was impossible my company would not be in business today. Lets focus on the topics so we can help people with their problems. Patrick
Electronics Forum | Thu Aug 20 07:10:46 EDT 2009 | davef
Questions are: * On what portion of the second side of the board [eg, solder only, solder mask only, etc] do you see this white hazy residue? * Could you attach a picture? * You mention cleaning this residue. What have you used to clean the residue?
winsouce.jpg)