Electronics Forum | Wed Jul 28 11:47:16 EDT 2004 | GCronin
I am looking for a consistent method of applying no clean liquid flux to solder pads. My main concern is if I use a standard air-over type dispenser mounted to an automated arm that the liquid flux will make a mess and not be consistent. I'm not to
Electronics Forum | Sat Oct 29 20:29:30 EDT 2016 | adamjs
Posting here because all the threads asking for feedback on it are locked. We have been extremely happy with the 4300 tacky flux for BGA attachment. Not only is it both washable and no-clean (i.e. wash-optional), it was also the only tacky flux tha
Electronics Forum | Wed Apr 03 19:03:31 EDT 2013 | hegemon
In agreement, in that you should have already printed enough paste on the board to accomodate the joint. Adding paste would give the result you described. (too much solder) Adding a little flux (only) and heat would be the correct path out of that s
Electronics Forum | Tue Nov 04 12:45:54 EST 2008 | smt123
Hi Martin, Have you considered printing the flux with a stencil? Stencils can be used for printing more than just solder paste. Quite regularly people use stencils for printing thermal grease, fluxes, conductive epoxy and more. The thing I like
Electronics Forum | Tue Aug 30 15:05:23 EDT 2005 | Shean Dalton
Dear Ing, Have you analyzed why some RF device aren't operational after washing? An assumption is that failures are related to the ultrasonic energy applied. Other possibilities are for poor rinsing, poor drying, inadequate washing on those failed
Electronics Forum | Tue Jun 15 12:03:27 EDT 1999 | Dave F
| Has anyone had issues where bottomside double reflowed smt has fallen off in the wave when using voc-free flux? I have verified the hotter profile was not the issue by using an alcohol based flux with no problems.This voc-free flux is also not caus
Electronics Forum | Thu Dec 29 10:41:42 EST 2016 | luciano
Thanks Evtimov, The flux is brand new and the amount of flux is enough and consistent across the surface of the boards.
Electronics Forum | Tue Feb 17 09:37:16 EST 2015 | charliedci
We made the same change a year ago, from foam to spray fluxer. One of the reasons we changed, to keep the acid number within specs (foam fluxing) we had to measure once or twice a day and add DI water to make up for evaporation, all along not able to
Electronics Forum | Mon Mar 25 13:48:52 EST 2002 | bcceng
We are currently applying solder bumps to hundreds of BCC's for rework. It is impossible to print to the PWB. It is recommended to apply solder bumps to the BCC's with 63/37 alloy making the rework faster and easier. Applying the solder bump on the
Electronics Forum | Wed Sep 15 05:15:24 EDT 2004 | Adam
I have chceked the fluxing application, I seem to be getting good consistent coverage across the board using our foam fluxing system. Good flux penetration on the top-side of the through-hole plating, as this was checked using a fax paper.There is no