Electronics Forum | Thu Jun 15 22:17:02 EDT 2006 | Thanagon
I'm now have target to flux saving. Could you please tell me. If we adjust level of spray fluxer nozzle up then we can saving cost of flux Quantity usage? What Others must adjust? such as pressure , flux flow. Thank you All for advise.
Electronics Forum | Fri Jun 16 08:37:51 EDT 2006 | Chunks
What type and brand of fluxer?
Electronics Forum | Sun Jun 18 21:41:58 EDT 2006 | Thanagon
Dear Sir, We used TAMURA type : TAF30-12DNS. This type nozzle can't moving up and down but we will modify that.Please comment that is O.K.? Regards, Thanagon
Electronics Forum | Fri Mar 22 14:19:38 EDT 2019 | gregcr
Thank you ProcEng1 Nordson sent me a flux suggestion list: No Clean: 1. Kester Select 10 2. ALPHA EF-2210 3. AIM FX-16 Water Sol: KESTER 2331-ZX Nozzle Tinning: SUPERIOR #75
Electronics Forum | Wed Dec 19 16:05:10 EST 2018 | ldavis
I created a spray fluxer for our wave solder years ago that is still working well although does consume a lot of flux and is also rather messy. It's cheap and easy though so what the heck, right? I just machined a manifold that will hold four BETE
Electronics Forum | Wed May 24 04:28:18 EDT 2006 | ge_lim
Hi Anyone use Warton Active '8' flux to clean the nozzle? Share me your experience
Electronics Forum | Fri Sep 04 02:09:03 EDT 2009 | sachu_70
Hi Walter, Do you refer to a sprayfluxer operation? The problem seems to be a parameter setting issue. 1. Ensure the wide angle spray reaches PCB with optimum jet pressure. You could pass a glass plate to understand flux coverage and view Jet pressur
Electronics Forum | Tue Oct 14 17:45:20 EDT 2008 | gregoryyork
is that the milky emulsion one ???
Electronics Forum | Fri Oct 10 05:04:26 EDT 2008 | bing007
We are using Mulicore MF101 flux and a Vitronics selective soldering machine on a lead-fee assembly and are having trouble with nozzles blocking even when the nozzle aperture is increased. Has anyone come across this problem before using fluxes with
Electronics Forum | Mon Sep 28 19:07:47 EDT 1998 | Steve Gregory
| I have had some field failures returned recently, the boards had flux contamination under the components in a sensitive area, Nothing really visible until the component was removed, and the board had no evidence of rework of any type. Is it poss