Electronics Forum | Sat Aug 02 08:12:05 EDT 2003 | davef
Q: So, can I concluded that this greenish "fungus" looking staff is not initiated from high hot air temperature setting ? A: Your temperature setting could have increased the growth rate of this crunchy looking stuff, but we wouldn't start there to
Electronics Forum | Fri Aug 01 23:43:52 EDT 2003 | Yngwie
Thanks Dave, the residue appeared to be similar to fungus. First, I thought it could come from water soluble flux but, our plant only runs no-clean. So, can I concluded that this greenish "fungus" looking staff is not initiated from high hot air temp
Electronics Forum | Thu Jul 31 11:33:51 EDT 2003 | yngwie
I faced problem over connecter's pin that were hot air soldered. This connector has 168 pins ( similar to the straddle connector ). The process is to apply the flux onto the connector's J-leads, and the hot air pencil were then ran thru' the leads to
Electronics Forum | Thu Jul 31 15:41:23 EDT 2003 | davef
Q: Could any of you guys tell me what exactly is this greenish thing ? A: No, but is not copper oxide. Copper oxide is brown, the color of a penny [here in the US] or an untreated copper laminated trace on a board. Many copper salts are greenish in
Electronics Forum | Thu Apr 01 21:18:31 EST 1999 | Chris Kelly
Glenn, There are both very good VOC-Free fluxes as well as alcohol based fluxes out there. This should be your primary focus if you are so lucky as to have to opportunity to actually select a flux! The use of nitrogen will benefit any no-clean pro
Electronics Forum | Tue Aug 22 10:53:45 EDT 2000 | Dr. Ning-Cheng Lee
Excellent question. Alloy development is relatively easy compared to flux formulation. New fluxes for Pb-Free alloys need upgrades in 2 critical areas: 1) thermal stability 2) oxygen barrier efficiency Since the Pb-Free alloys require reflow proce
Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Wed Sep 22 02:45:23 EDT 1999 | Brian
| | Dear All, | | | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | | | I mean that I wonder
Electronics Forum | Mon Nov 12 18:08:37 EST 2007 | samir
That's when you give that "Supervisor" a tall glass of SHUT THE F*CK UP. I betcha you regret even mentioning it to him. I'd have just made up some techno-babble and switched it regardless. Told him something like - "pure IPA will act as a catlyst
Electronics Forum | Thu Mar 12 22:32:49 EDT 2015 | louisg
Hello. I would like to know the difference (if any) between water soluble flux and test socket cleaners (e.g. for Burn-In Board test sockets). As far as I know, they both remove oxides (tin & copper) with an activator, solvent and surfactants. Tha