Electronics Forum | Thu Oct 15 16:39:07 EDT 1998 | Dave F
Steve: I thought Kyzen products were "additives" to either aqueous or semiaqueous inline or batch machine cleaning processes. I'm trying to clean the no-clean residue from a few components that can not bear to see water. Can you use Kyzen products
Electronics Forum | Tue Jul 03 01:54:42 EDT 2018 | rdhiman1
Reaching out to all conformal coating experts, please help! While setting up conformal coating using the automated atomized spray, we observing issues associated with conformal coating wetting on the following regions: 1) Component edges 2) Metalli
Electronics Forum | Fri Jan 08 17:56:16 EST 1999 | Eric Miller
Hi Chrys, Hate to bring you down, but, wave solder pallets exposed to any kind of flux is subject to "Build up" on the carrier. You still have to clean them, hopefully on a regular basis.If the pallet is being run in a high production envirnment, I w
Electronics Forum | Fri Feb 20 08:56:42 EST 2004 | davef
We successfully clean WS flux on 1mm and 1.25mm pitch BGA. For 0.8mm pitch BGA, we use no clean, because we cannot remove the flux residue from under them efficiently. Use ion chromatography testing to be sure it is clean under the BGA. IC is the on
Electronics Forum | Tue May 03 10:57:22 EDT 2005 | Frank R.
We received about 5K assembly boards from china. They left flux residu on top of the board and the flux they use was different than us. RESULT ... we use a translucent cylicon to cover the board and it was not possible to dry the cylicon because of
Electronics Forum | Mon Nov 22 17:32:34 EST 2004 | davef
Assemblers often assume that the board and component suppliers provide them with clean product. This was not a problem when everyone used water washable fluxes, because the water washing used to clean the flux residues also cleaned the board and com
Electronics Forum | Sun Nov 22 09:36:17 EST 2009 | patrickbruneel
Dave, A low residue/No residue flux does exist that when an excessive amount of flux is applied it would only create a cosmetic problem not a reliability issue. The active ingredients are neutralized by the heat applied in the soldering machine and
Electronics Forum | Tue May 26 14:10:24 EDT 1998 | Ryan Jennens
We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localized to just t
Electronics Forum | Tue Jun 14 17:32:44 EDT 2011 | davef
It depends on the flux and the down-stream processing ... * If there is adequate down-stream cleaning: We are ambivalent. * If the flux is low residue and there in no down-stream cleaning: We don't like using a syringe because it squirts liquid flux
Electronics Forum | Thu Jun 07 08:55:01 EDT 2007 | grics
Well... Some are worse than others... How can you identify that it is caused by uncured mask and not flux residues? The flux is from indium, 3592. Some research in their tech library revealed that either Kyzen or Zestron would work, which is the re