Electronics Forum | Tue Nov 04 09:35:43 EST 2008 | Martin
We are using tucky flux Alpha UP78
Electronics Forum | Fri Apr 13 15:42:18 EDT 2007 | flipit
This is sort of interesting. We had a clock problem with Alpha OM-338 lead free paste. The flux residue was causing a clock problem and the clock was only a few KHz. We went back ot OM-5100 lead paste and the problem never occurred again. Chris
Electronics Forum | Fri Apr 13 12:24:07 EDT 2007 | teamcanada
We assemble for a customer that is having an inconsistent low level analog interference we believe with the no clean flux residue from Alphas OM5100 solder paste. We are considering testing Amtechs 4300 water washable no clean paste. We will test bot
Electronics Forum | Fri Apr 13 17:11:12 EDT 2007 | jmelson
Even though this is a "no clean" flux, are you (or the customer) cleaning the boards? If this is truly a low signal level device, there is no way you will get away without cleaning the flux residue. I do a lot of low-level hardware, and we have to
Electronics Forum | Wed Mar 22 17:28:13 EST 2000 | Steve Harshbarger
Donnie, It's funny you ask this question. I just last month was at a company doing exactly what you are asking (Alpha 310 flux with infrared heating). They were successful, but they had 2 important things going for them. 1) A spray fluxer that wa
Electronics Forum | Thu Oct 13 15:41:30 EDT 2005 | lyrtech
Hi, We have a customer who give us a 20K board contract each year. It's only thru-hole components.The baord is HASL plated. So we pass it into our wave. No problems. Recently, our customer decided to go into GOLD PLATED finish. We take the same re
Electronics Forum | Tue Apr 29 15:45:09 EDT 2003 | davef
We have mixed bar solder from alternate suppliers in our wave soldering machine. Issues that you need to address before changing your solder supplier are: * Assure that the alloys are the same. In this, consider imaginative people may be reporting