Electronics Forum | Fri May 03 16:06:44 EDT 2013 | hegemon
To be short, no change in profile is going to get you through this. As I recall the point of hard gold is to retard the wetting process, so no surprise here. For example a connector might have hard gold plating at the mating surface, but not at t
Electronics Forum | Mon Jun 12 07:42:56 EDT 2006 | brian.perry@suntroncorp.com
We are placing a gold plated device (LCC) to a NiAu PCB using a SnPb No-clean solder. We're noticing quite a bit of difficulty with reliable joints (intermittent connectivity) and if we have to rework a particular device, adjacent devices of this sa
Electronics Forum | Wed Jul 12 11:26:12 EDT 2006 | flipit
Hi, I believe you have classic gold imbrittlement here. With 80 microinches of gold you are way over the limit. You can try to reflow longer time and at a higher temperature. The gold does not melt into the solder joint. The gold dissolves into
Electronics Forum | Mon May 20 15:43:01 EDT 2013 | ngotranbestek
Hi I meet problem by PCB with diameter 300cm and thick 6mm i used tin-lead with profile normal, soak time 60-90 sec, Temp peak is 220 degree C, But solder see not good, not shiny. Any body recomend help me to fix this problem for Hard gold playing.
Electronics Forum | Thu May 02 09:33:30 EDT 2013 | 15009
Looking for advice on soldering lead free paste to a board with very heavy gold plating. I have learned from the Customer that this is HARD GOLD and that it is 10-20 Micro Inches Hard Gold over 100 Micro inches of Nickel. When we reflowed the solde
Electronics Forum | Sat Apr 14 09:28:58 EDT 2007 | davef
When soldering a component to a board, the solderability protection on the component combines with the solderability protection on the board and the solder to form an alloy. This alloy is unique for that combination of solder and solderability protec
Electronics Forum | Mon May 12 23:28:33 EDT 2003 | dehlers
To the best of my knowledge and experience the 2 % Ag component is not for embrittlement but rather to reduce gold scavenging caused by the propensity for tin to react with the gold. I have seen eutectic tin/lead actually disolve gold wire after a f
Electronics Forum | Mon Dec 13 10:12:45 EST 1999 | John Thorup
Hi Dennis The gold plating on a circuit board is present to protect the nickle plating from corrosion. The layer is so thin that as it goes into solution in the solder it constitutes only a small percentage of the total joint. It is commonly accept
Electronics Forum | Tue Dec 07 16:34:54 EST 1999 | Russ
Wolfgang, I appreciate your continued feedback! The main reason that I shortened the Time Above Liquidous (TAL) was it appeared that I was burning off all of the flux from the paste. By shortening the TAL to 45 seconds and decreasing peak temp to
Electronics Forum | Tue Dec 07 08:11:04 EST 1999 | Wolfgang Busko
Hi Russ, there�s something I don�t understand about the measures you took. I guess that TAL means time above liquidous and shortening of that time can result in bad dissolution of the protective Au-layer. The necessary time for the Au to mix with you