Electronics Forum | Thu Dec 23 15:29:48 EST 1999 | Glen Robertson
Mike - I'm not in the EMS business, but I suspect most of them are very reluctant to reveal much about their quoting process. You might want to try some of the third-party data suppliers like Ceeris (www.ceeris.com), and you can also check the C
Electronics Forum | Tue Dec 21 13:27:47 EST 1999 | Vince Whipple
Charlie: As far as setting up a spray fluxer.. Are you spraying no-clean, voc free, water soluble? What you would want to do is to run a blank pcb through the fluxer and pop it out before the preheaters. Visually inspect for variations in uniformit
Electronics Forum | Sun Jan 05 14:45:23 EST 2003 | Brian
I don't think it is a good idea to run your own board in house. The cost will be higher than let the contract out company do it for you. If you are looking for a Smt line.. You must spend atleast $400.000 for an use equipment. Printer= $100.000 Pick
Electronics Forum | Mon Dec 20 07:09:03 EST 1999 | Christopher Lampron
Ron, The simplest way to process fexible PCB's that I have found is to use a process carrier fixture. There are companies that manufacture process carriers that are capable of holding flex through stencil, placement and reflow. The carriers are capab
Electronics Forum | Tue Dec 14 20:57:07 EST 1999 | Curtis T.
John, I have never seen black pad covering a majority of the board, that would be a scarry thought. I think he is talking about building modules (sims dims) and getting soldering spatering on the gold edge connectors. We went the rounds with that s
Electronics Forum | Tue Dec 14 10:36:42 EST 1999 | Paul Peterson
I recently encountered reflow soldering defects on a pair diode package, the smd pad had a green contamination, I'm convinced that this is not oxidation. The no-solder condition appears to be caused by a sloppy soldermask process, although over the y
Electronics Forum | Sat Dec 04 09:33:18 EST 1999 | Christopher Lampron
Hello Russ, I believe that the dullness in color of the solder joint is related to the gold finish on the pads. I have had done alot of thru hole soldering of gold pins as well as SMT on gold finish and have seen the condition that you are talking a
Electronics Forum | Fri Dec 03 14:33:18 EST 1999 | John Thorup
Hi Cunli I guess it's too much to hope for that you're back but it's nice that you're still paying attention . I've used the printer friendly version before and it worked fine. However it does't always work. I'm holding Dave F's posting (help with
Electronics Forum | Tue Nov 30 15:38:27 EST 1999 | Wendy Casker
Hi, I am looking for land patterns for 0612 and 0508 chip capacitors. Because they are not standard (yet) package sizes, i am having trouble finding a standard land pattern. (If you don't know what these are, picture a 1206 or an 0805 with the te
Electronics Forum | Mon Nov 29 16:17:43 EST 1999 | Curtis T.
Are these blades coated with something like PTFE (teflon)? If so does the coating flake off over time. Incidently I just got a pice quote and they are 4.5X that of our standard MPM nickel plated spring steel, so I wanted to make sure they would last