FR-4 will be OK for small products such as cellular phones. Here the temperature gradient across the board may be 3-4C only, and the board temperature can be well controlled. At temperature above around 245C, the discoloration and delamination may be
Electronics Forum | Tue May 12 10:02:52 EDT 2009 | dwl
I am trying to develop a process for building high environmental temperature PCBs (150-225C) specifically for down hole applications. I'm specifying an evaluation board and was thinking about using polyimide PCBs with Sn05Pb92.5Ag2.5 solder. What so
Electronics Forum | Thu Oct 07 14:40:31 EDT 1999 | Carol Zhang
I have a board, 4 spacers needed to be soldered on the board first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will be no p
Electronics Forum | Tue Aug 22 13:04:04 EDT 2000 | Eugene Smelik
Dr. Lee, Given the higher reflow temperatures for Pb-Free assembly, will common FR4 laminate materials be adequate, or do you believe that higher glass content boards will be required for mainstream Pb-free assembly? As a corollary question - if man
Electronics Forum | Thu Sep 04 02:43:09 EDT 2008 | benefon
Thanks This error only occurred with one oven profile with the reflow zone temperature set at 270�C. Perhaps it really has to do with the exhaust pull as the oven is operating very near its temperature limit with this profile. I will check that. Tha
Electronics Forum | Thu Oct 07 15:39:59 EDT 1999 | Carol Zhang
| I have a board, 4 spacers needed to be soldered on the board | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will b
Electronics Forum | Tue Sep 02 13:35:29 EDT 2008 | evtimov
Hi, I don;t thing there is an overtemperrature sensor. Just the thermocpouple returns a higher temp(voltage) to the controller and your software goes to alarm, cooldown or what ever it does. Emil
Electronics Forum | Fri Oct 08 16:48:57 EDT 1999 | Dave F
| I have a board, 4 spacers needed to be soldered on the board | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will b
Electronics Forum | Tue Oct 12 08:48:16 EDT 1999 | Carol Zhang
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Wed Sep 03 07:39:19 EDT 2008 | pjc
You may not be getting enough exhaust pull, so the cooling modules over temp. Try swapping blower motors to isolate that before buying one. STANDARD AIR OPERATION: - Load-end: 150 cfm (255 m3/hr) at the 4� (102 mm) stack (minimum requirement) - Unlo