Electronics Forum | Fri Aug 11 15:01:24 EDT 2000 | g cronin
I am looking for a storage system for short term storage of open BGA's or longer term de-humidifying or moisture removal.. Is there any low humidity chambers available??? greg
Electronics Forum | Fri Nov 20 08:51:34 EST 2009 | Sean
Hello, This is interesting topic that I would like to share and discuss with you.. I came across few projects from various SMT factories where its product(Computer) reach field, experience No Post/boot defect. This problem become very obvious when
Electronics Forum | Tue Jul 06 08:48:11 EDT 2010 | Sean
Hi all, Is anyone used to encounter PTH(plated through hole) crystal component(Not SMT component) become malfunction when the environment humidity is more than 90%? It is happening here...It is very weird that crystal become OK when humidity is bac
Electronics Forum | Fri Nov 20 14:50:13 EST 2009 | davef
One of our instruments has a high impedance front-end. We: * Passed functional test in the environmentally controlled shop. * Failed test, on the same unit, while carrying it to burn-in chambers in an uncontrolled part of the plant. Solder flux resi
Electronics Forum | Fri Apr 24 16:06:31 EDT 1998 | JOHN MCNALLY
I am looking for installation guide or manuals for a 1982 mod#16607 constant humidity & temp chamber. Ransco does not have one, nor does Despatch the company that bought this product line. If any one out there has any manuals that might be of some he
Electronics Forum | Fri Aug 09 18:06:54 EDT 2024 | arminski
Also Humidity Chambers can go below 20% RH Only.
Electronics Forum | Tue Jul 27 08:03:55 EDT 2010 | scottp
You have to figure this out for yourself for your paste. When I evaluate solder pastes I require good tack, no solder balls, and proper wetting after 4 hours at "reasonable" ambient conditions. I also print boards and put them in a temp/humidity ch
Electronics Forum | Sun Nov 22 19:53:10 EST 2009 | prodrivegsr
Hi Ju Yong, The PCB are dry in an airseal cabinet(Staging Chamber) before IR Oven. The bubbles show at around body and solder joint area. You mean the moisture will create bubbles ? Able to advice the humidity and temperature that you are using in
Electronics Forum | Wed Apr 06 04:18:03 EDT 2011 | emmanueldavid
TK, Hope you got it right only for this round of assemblies. Well, passing through a Reflow belt is not an ultimate process to dry circuit cards & take out moisture from Solder finished layers. First of all, if the packs were not unsealed (even s
Electronics Forum | Wed Aug 21 17:44:32 EDT 2002 | davef
Splitting hairs, I expect SIR of all solderability protection, including OSP, to decrease after reflow. What�s more, I expect the SIR of all solderability protection to pretty much decrease over time. The �comb pattern� test specimens meet requirem