Electronics Forum | Mon Aug 09 07:13:08 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problemsd
Electronics Forum | Tue Aug 10 01:02:31 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problems
Electronics Forum | Wed Feb 10 08:10:26 EST 2010 | davef
Here is a posting by P Kinner at Humiseal ... Typically, there are three main approaches to avoid coating wicking into press-fit connectors (and other keep out areas). Wicking is a phenomenon caused by a combination of low viscosity of conformal coa
Electronics Forum | Fri Feb 05 20:39:41 EST 2010 | localperm79
I've recently been placed in control of operations of our SCS conformal coat sprayer and I must eliminate problems with wicking of humiseal 1b73 into surface mount connectors while also trying to minimize masking as much as possible. We use a 55:45
Electronics Forum | Mon Dec 27 10:03:35 EST 2010 | duso02
Contact your distributor for the coating or Humiseal directly. Humiseal has had a recent issue with batches of 1B31. The specific problem is lack of adhesion, which is what you have as well. You need to find out if your batch # is one of the affected
Electronics Forum | Mon Jan 03 00:30:30 EST 2011 | raghu
Contact your distributor for the coating or > Humiseal directly. Humiseal has had a recent > issue with batches of 1B31. The specific problem > is lack of adhesion, which is what you have as > well. You need to find out if your batch # is one >
Electronics Forum | Sat Aug 07 02:28:20 EDT 2010 | raghu
We have PVA 350 benchtop dispensing equipement with humiseal 1A33 CC material. is there any moisture measurement process in conformal coating material?
Electronics Forum | Fri Apr 17 14:08:00 EDT 2015 | davef
Humiseal says, "UV cure – These materials are also more difficult to repair as they are the most chemically resistant and mechanically tough of all conformal coatings. Removal is possible locally by using powder abrasion."
Electronics Forum | Mon Dec 28 09:12:56 EST 2009 | kpm135
@tommyg_fla According to the TDS the recommended coating thickness for Humiseal 1B31 is only 1-3 mils so if I had to guess I would say your issue might be that you're re-coating over the first pass too soon. All the solvent hasn't evaporated and the
Electronics Forum | Fri Feb 18 11:25:14 EST 2005 | davef
It's weird that it would be just 0805. When we see this it relates to a single part number and it goes way after a time. We use a Humiseal 1B73. I've emailed you the contact for a person that is very knowledgeable on conformal coatings.
.gif)