Electronics Forum | Wed Oct 17 02:04:39 EDT 2018 | robl
SCC3 has an operating temperature of 200C, as long as it is heat cured at 100C. https://www.electrolube.com/pdf/tds/044/DCA.pdf It's also a silicone so needs to be coated & cured away from anything you value. Otherwise there are plenty of PU's and
Electronics Forum | Fri Mar 20 10:31:19 EST 1998 | Mick Jones
| I will be starting a conformal coating process soon, I am looking for any pointers on | 1) Best method for masking components, tape mask, liqued mask | 2) Which is best Spray or Dip? | 3) Compatiblity with no clean solder paste (flux residue) | I h
Electronics Forum | Mon Dec 28 09:12:56 EST 2009 | kpm135
@tommyg_fla According to the TDS the recommended coating thickness for Humiseal 1B31 is only 1-3 mils so if I had to guess I would say your issue might be that you're re-coating over the first pass too soon. All the solvent hasn't evaporated and the
Electronics Forum | Tue Jul 31 10:16:59 EDT 2012 | silverbullet
We are in the process of revamping our conformal coating room. Presently, we have a C-740 Nordson Asymtek coating machine that sprays most of our boards with Dow Corning 2577. We are spending a lot of time masking boards and are thinking of upgrading
Electronics Forum | Mon Jun 25 11:55:47 EDT 2007 | ck_the_flip
I don't think THEY (Humiseal) know how their material cures. I have a data sheet from them for 1B73, and it says 24 hours at room temperature or 30 min. @ 170�F. We use our in-line oven mainly to dry the material and make it tack-free. You would
Electronics Forum | Wed May 11 15:30:12 EDT 2005 | amejia
The problem is that we don't use a wave solder machine. Our process right now is that we mask the holes, let it sit at room temperature until it dries, then conformal coat the boards with Humiseal. And, we cannot have the boards ready the day befor