Electronics Forum | Wed Jun 14 10:15:08 EDT 2017 | cyber_wolf
Nitrating is new to me too. I assume it means nitride coating.
Electronics Forum | Mon Mar 30 12:57:06 EDT 2020 | emeto
IPA is 99% Alcohol, so i assume should be more than enough.
Electronics Forum | Thu Jul 22 17:26:16 EDT 2021 | proceng1
Spray or foam? Are you looking for IPA or Water based?
Electronics Forum | Sat Jul 02 10:35:55 EDT 2022 | madisreivik
What kind of cleaner did you use ? Alcohol/ IPA probably does not work.
Electronics Forum | Thu Jun 20 16:24:59 EDT 2002 | blnorman
At the OSHA training institute, our instructor stuck an electric drill in a bucket of water to demonstrate what proper grounding will do. Personally I wasn't going to try it. All our fluxes are no-clean, and are IPA based. Granted we used aqueous
Electronics Forum | Sat Mar 29 08:50:30 EST 2003 | davef
Barry Echoing an earlier poster, replace your stone. Use the suppliers' recommended thinner. Do NOT use isopropanol [IPA]. IPA contains water. Water is the bane of low residue soldering. It will get you in trouble fast. From IPC, get your hand
Electronics Forum | Thu Sep 28 10:49:47 EDT 2006 | pavel_murtishev
Good afternoon, We use PD955M daily and are also happy with PD955M. Consider PD955�s printable version: PD955 PY or PD955 PR (difference is only in color: red or yellow). Do not use IPA for cleaning. IPA tends to harden adhesive making cleaning extr
Electronics Forum | Tue Jul 29 22:13:59 EDT 2008 | davef
IPA is a fire hazard. Be sure your fire extinguishers are charged and your evacuation plan is current, when using IPA in the vacinity of a wave solder machine. Have you tried DI water? Solutions used in wave finger cleaners include: * Techspray SMT
Electronics Forum | Sat Dec 03 17:21:45 EST 2011 | davef
We can't tell much from your pictures, except there are rounded gray blobs that could be solder. If that's the case, you need to get that solder hotter. Please give us the temperature readings of those blobs during reflow. You mentioned that you're
Electronics Forum | Wed Oct 05 04:32:49 EDT 2016 | piyakorn
Rinse IPA 5 Min --> Treathment/soak IPA50%+SILENT50% 5Min --> Baking 60C/30Min --> Parylene coating (around 8Hr in chamber) --> Found defect spot. We have simulated and ensure board drying before parylene that still have spots. Need help - Thank y