Electronics Forum | Tue Jul 23 15:41:31 EDT 2002 | habs24
Does anyone have any information or experience soldering of class 3 products with WS fluxes. We are currently leaning toward Alpha WS609 flux, however the customer's interpretation of J-Std-001C feels that type 'H' fluxes (WS) are not allowed. Any
Electronics Forum | Wed Jun 20 19:52:47 EDT 2007 | davef
J-STD-001, 5.4 Solderability Maintenance states words to the effect "The manufacturer shall ensure that all components [bla bla bla] are solderable at the start of hand and/or machine soldering operations." So, how many you contractor cats 'n kittie
Electronics Forum | Tue Nov 15 16:31:04 EST 2011 | pcbrown
Can anyone tell me if the Metcal SP200 solder station meets the J-STD-001 Rev E requirement of holding a tip temp of +/-9F at rest? I am in a fight with an auditor over this. These irons do not require calibration but I need to know if they meet J-ST
Electronics Forum | Thu May 23 07:50:04 EDT 2013 | icin
The attached images appear to be a result of a touchup process. We believe that this is not a fracture, but more of a condition where the solder touchup process did not completely flow the solder. Is this acceptable per J-STD-001 and IPC-A-610 Class
Electronics Forum | Mon Jul 24 07:18:51 EDT 2017 | jamesbarnhart
IPC has updated assembly standards for IPC A-610 and IPC JSTD-001 making them easier to use and adding information in areas that have evolved. Both IPC J-STD-001E and IPC-A-610E have also been more closely linked to eliminating the differences that c
Electronics Forum | Mon Jul 24 09:15:32 EDT 2017 | davef
James: This is not "breaking news." IPC-A-610F, Acceptability of Electronic Assemblies was released in July 2014. Both, ... * IPC-A-610G, Acceptability of Electronic Assemblies * J-STD-001G, Requirements for Soldered Electrical and Electronic Assem
Electronics Forum | Wed Aug 06 20:50:42 EDT 2003 | davef
Well, if it "keeps coming up", let's take a pass at keeping down. For: * Requirement that gold be removed from components, pads, etc. is J-STD-001C, 5.4.1 * Context of that requirement [J-STD-001C, 5.4.1] and 6 or 7 references are in IPC-HDBK-001.
Electronics Forum | Thu Sep 26 14:43:43 EDT 2002 | Jim M.
unsure of what solder spec. your working to?.IPC/EIA J-STD-001C, Section 9.2.4 clearly states dull, matte, gray or grainy appearing solders are accpetable depending on your process and if the acceptability of the neaxt paragraph is met.IPC 610 and J-
Electronics Forum | Mon Apr 16 09:12:23 EDT 2007 | davef
Standard for appearance: J-STD-001 and IPC-A-610 committees eliminated the requirement that solder connections be "bright and shiny". Certain solderability protections; such as Au, NiPd, NiPdAu; can affect the surface texture of a solder connection,
Electronics Forum | Wed Jul 18 10:35:41 EDT 2007 | hussman
This seems like an odd request from an auditor. I can see an auditor requiring proof that you meet the J-Std, but verify? This would require you purposely damage product on a "before and after" scenario. As long as your manufacturing guideline say