Electronics Forum | Wed Nov 02 12:08:40 EST 2005 | chunks
It could be lack of preheat or flux. You can verify the flux by hand applying. I'll bet it's lack of preheat though. That's usually the case with selective solder.
Electronics Forum | Mon Jul 17 11:40:20 EDT 2006 | Chunks
It's been a few years, but lack of preheat was my problem with this machine.
Electronics Forum | Fri Jan 05 17:25:30 EST 2024 | ankitgun
My company recently acquired the Vitrox-V510 Optical Inspection Station, equipped with the 'V510 Series' software. However, I've noticed that the software appears to be outdated and doesn't meet modern standards. It lacks a comprehensive component li
Electronics Forum | Wed Mar 21 16:19:23 EST 2001 | mparker
Having re-read my message I do not know where you deduced "quick", unless you are taking "minimize mean time to trained and effective" as being I want the fast food version. What I mean is what you already agree with, make the information available
Electronics Forum | Thu May 10 14:43:47 EDT 2012 | davef
fluxer => cleaning (or lack there of) => conformal coating: there is a lack of compatibility. You need to figure-out which is the bad boy. Maybe a good guess is to conformal coat boards at each step in the process and then have them tested. Don't de
Electronics Forum | Tue Aug 06 07:07:31 EDT 2013 | sarason
My software does offline generation of Samsung files specifically the CP45, SML421 and the SSA file format files. It is shareware. If you are interested in other Samsung formats I do have files for other models I have not added due to lack of current
Electronics Forum | Wed Mar 22 12:53:43 EST 2000 | David Spilker
Be careful if you use Ni/Au. The "black pad" phenomenum can be crippling. We moved from Ni/Au to OSP because of it. I also don't want to return to the lack of flatness of HASL.
Electronics Forum | Tue Nov 14 06:30:53 EST 2000 | colin marshall
I am at the early stages of investigating how we could track our m/c feeders. Obviously the theory of this is quite simple but I am finding a lack of information on the net. Could anyone suggest a method or software package for this purpose.Any info
Electronics Forum | Wed Mar 22 12:53:43 EST 2000 | David Spilker
Be careful if you use Ni/Au. The "black pad" phenomenum can be crippling. We moved from Ni/Au to OSP because of it. I also don't want to return to the lack of flatness of HASL.
Electronics Forum | Sat Feb 28 01:02:45 EST 1998 | Ray
Notice the lack of response to the laser system comment? Unspoken words can say a quite a bit...they don't want to have to address the issue. I wonder why? Ray