Electronics Forum: lead free pth components to leaded process (Page 1 of 2)

Changing Ni/Au finish to HASL lead free

Electronics Forum | Wed Dec 22 07:20:21 EST 2010 | piter

HI I used both of solder leveling HASL and ENIG, HASL I can recommended for biger pitch is cheaper solder leveling than ENIG but problem with that solder leveling is during the reflow process HASL isn't flat and during reflow process component move

Nonwetting Components - why won't components wet to solder?

Electronics Forum | Thu Jan 25 13:20:17 EST 2007 | slthomas

Are you running a lead free process? If not, have you identified these as lead free components? If so, have you increased the temps in your profile to accomodate that? After that, I'd look for a AgPd (silver/palladium) or some other such PITA platin

Reliability assessment SnPb joints to lead-free component

Electronics Forum | Tue Jun 07 19:24:26 EDT 2005 | Joseph

Dear all, Recently we encountered some functionality failure when using lead-free component(Sn99.3/Cu0.7)at SnPb(Sn63Pb37) wave soldering process. Can lead-free component use at non-lead free process? Any input/idea are much appreciated. Rgds

where to get good flux

Electronics Forum | Wed Apr 03 19:03:31 EDT 2013 | hegemon

In agreement, in that you should have already printed enough paste on the board to accomodate the joint. Adding paste would give the result you described. (too much solder) Adding a little flux (only) and heat would be the correct path out of that s

Soldering Lead-Free Globtop BGA to Pin-Socket Interposer

Electronics Forum | Wed Nov 19 16:35:27 EST 2003 | davef

We'd be incluned to dip the BGA ball in tacky flux, place the BGA on the PTH interposer, reflow that suka, and get on with things. [Take the people involved out to lunch with the money you save on not buying a stencil.] On damaging the glop top, we'

Restructuring Rework Process - Back to Basic

Electronics Forum | Tue Feb 01 14:26:34 EST 2005 | rabell

I agree re; "always will be some assemblies that must be repaired". This is unlikely to lessen in the near term with an imminent move toward Lead-free. We are currently working with Cookson, PACE, and BEST developing a course in lead-free rework wh

Reliability assessment SnPb joints to lead-free component

Electronics Forum | Thu Jun 09 06:15:17 EDT 2005 | Clampron

Joseph, We have all been using lead free components for some time. Many passive already have a Pb free plating and we have not seen catastophic failures on them. From the information I have seen, I think this should be OK (with the exception of BGA'

Reliability assessment SnPb joints to lead-free component

Electronics Forum | Thu Jun 09 05:04:05 EDT 2005 | Joseph

Dear Patrick, Unfortunately we do not know what exactly the failure as our customer refuse to reveal to us. From visual inspection the solder joints are smooth and shiny as per IPC-A-610 requirements. The component supplier (IR) commended that they

Re: Adding leads to leadless parts

Electronics Forum | Sun Dec 19 08:05:14 EST 1999 | Dave F

Clarissa: We've all done thing on a limited basis, especially on prototype boards, but this doesn't sound like a limited basis, or prototype boards. (And may be I reading too much into this, we all know the frailities of conversing like this.) Thi

omit stencil apertures to hand solder or paste, reflow then solder.

Electronics Forum | Thu Feb 27 02:55:53 EST 2020 | hexton

I want to avoid peoples preferences as they will differ and will not be a deciding factor. A heat gun will introduce risk to surrounding PTH components and having to add protection for those, will limit any gain in productivity. There is no question

  1 2 Next

lead free pth components to leaded process searches for Companies, Equipment, Machines, Suppliers & Information

IPC Training & Certification - Blackfox

Component Placement 101 Training Course
convection smt reflow ovens

We offer SMT Nozzles, feeders and spare parts globally. Find out more
SMT feeders

High Precision Fluid Dispensers
SMT feeders

High Throughput Reflow Oven
Circuit Board, PCB Assembly & electronics manufacturing service provider

Software programs for SMT placement and AOI Inspection machines from CAD or Gerber.
design with ease with Win Source obselete parts and supplies

"回流焊炉"