Electronics Forum | Mon Jan 26 19:51:48 EST 2004 | davef
You should be able to obtain a smooth finish. A "glass-like finish" is in part a function of the coating material, assuming good process. When we see "orange peel" conformal coating, we think moisture from the spray room environment, conpressor, et
Electronics Forum | Mon Jan 26 05:45:51 EST 2004 | Sam
Does anyone know, what causes the orange peel affect when spraying pcbs with conformal coating ? Are there ways of minimising or eliminating this ? Is is possible to achieve a glass like finish ? if so how Thanks Sam
Electronics Forum | Mon Nov 27 13:36:41 EST 2000 | C.K.
You'd more than likely have repairability issues with the Acrylic based one. The acrylic-based finish is alot harder and more brittle versus the silicone. Some of the new silicones, you can just "peel" with your fingernail, while still getting reli
Electronics Forum | Sun Dec 26 23:48:01 EST 2010 | raghu
Dear Sir, We are using 1B31 conformal caoting of 48 sec viscosity in Zahn #1 cup, by machine(PVA354) application with Tank air pressure 2.3 psi, automising air pressure 1 psi. 7 days after application we are observing peeling off problem.. And n
Electronics Forum | Tue Feb 10 13:59:29 EST 2004 | Vadim
At times the orange peel effect can be from excess flux improperly removed. Our company strictly provides the service of selctive conformal coating application. We quite often see this. Most times if the board is simply "water washed", or IPA washed,
Electronics Forum | Tue Feb 10 14:02:03 EST 2004 | Maryann
At times the orange peel effect can be from excess flux improperly removed. Our company strictly provides the service of selctive conformal coating application. We quite often see this. Most times if the board is simply "water washed", or IPA washed,
Electronics Forum | Fri Jul 24 16:39:16 EDT 2015 | cnotebaert
have done it in the past, used silicon as it will flex,, however its not the most robust material! tends to peel/flake off.
Electronics Forum | Tue Jun 02 14:32:58 EDT 1998 | Chris Fontaine
We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not alwa
Electronics Forum | Wed Jun 03 01:06:13 EDT 1998 | Mike Moninger
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Tue Jun 02 15:53:32 EDT 1998 | Earl Moon
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al