Electronics Forum | Wed Jan 21 16:55:22 EST 2004 | patrickbruneel
Hi, Are you testing bare boards or soldered boards. Are the test probes in contact with soldered pads or contacting the copper with the osp coating (not soldered). If you could clarify this it would be easier to give some hints for probable causes.
Electronics Forum | Tue Sep 26 20:19:51 EDT 2000 | Dave F
Never heard of N-Tech. Whose material do they use? Two common materials are: Imidazole (Via Systems) and Entek (Enthone) OSP is a lacquer that fabs apply to boards by either spraying or dipping. What thickness control does your fab use? For inst
Electronics Forum | Tue Sep 26 08:41:27 EDT 2000 | greg
I am processing PCB's that have an n-tech osp coating and am finding huge inconsistencies in wetting. Some boards process clean with good wetting and the next has terrible wetting. The boards are stored and handled properly. Has anyone had this
Electronics Forum | Mon Aug 28 13:38:09 EDT 2006 | Steve
What kind of lead free board? ImSn, ImAg, ENIG, OSP?
Electronics Forum | Mon Aug 28 17:04:52 EDT 2006 | Board House
ImSn - Immersion Tin - Not Recomended- short shelf life ImAg - Immersion Silver - Prefered Surface finsh by most Board houses, Best reworkablility, 12 moth self life, ENIG - Electroless Nickel Immersion Gold - Second Choice for Board Shops, 12 -
Electronics Forum | Wed Sep 06 17:13:17 EDT 2006 | Board House
PB-free Hasl was not mentioned due to the following: 1)Equipment Convertion at the PCB Manufacturing side is expensive. 2)You are subjecting the PCB to Higher Temps than Std. solder. 3)Most PCB Houses are not going to invest in Two Hot Air level
Electronics Forum | Tue Aug 29 11:22:12 EDT 2006 | yuceltemel
Dear Bruce, We had the same problem in the same condition. Every compnent and the PCB (OSP) has changed as lead-free and we need to solder them with SnPb. For solution we have increased the flux amount applied on PCB and the pre heat zone temper
Electronics Forum | Wed Jul 01 11:19:50 EDT 1998 | Earl Moon
| I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built some
Electronics Forum | Thu Jul 02 15:23:15 EDT 1998 | Justin Medernach
| | I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built som
Electronics Forum | Fri May 31 10:35:46 EDT 2002 | dason_c
I think that the IPC spec only apply to the MSD. I had a paper from Lucent and forwarded by Francois Monette, please aware that the first 2 hours, the moisture doesn't bake out from the assembly/component and result show that it is increase the weigh