Electronics Forum | Tue Sep 11 22:52:18 EDT 2007 | davef
Here are some options for removing OSP coatings from pads of the BGA substrates. * Leave the substrates in storage for 13-14 months. Shelf life of OSP coating is ~12 months, depending on the product. * Wash the substrates in your aqueous washer. Ea
Electronics Forum | Mon Sep 10 23:13:08 EDT 2007 | weehn
hi, i'm from the semicon (BGA assembly). Could you advice what is the best method / procedure to remove OSP coatings from pads of the BGA substrates. thanks Wee
Electronics Forum | Sat Dec 30 04:23:50 EST 2023 | 012band
I have used LTS (Sn57.6%Bi0.4%Ag) solder balls for soldering on Ni/Au pads, and I have observed a wrinkle pattern on the ball surface. When you attempted soldering on CuOSP substrate pads under the same conditions, the surface appeared normal. Additi
Electronics Forum | Thu Apr 14 17:24:06 EDT 2022 | cbart
depends on board finish and PCB substrate materials. If you were using OSP or silver finished bare boards the time to process is less than an ENIG or HASL finished. certain substrate material absorb more moisture than others or at a quicker rate. so
Electronics Forum | Fri Dec 12 11:52:59 EST 2003 | Marc Simmel
I have encountered problems with a 90/10 tin-lead plated SMT component wicking all the solder paste off the pads on the substrate. Worst, the defect occurs randomly - adjacent leads may have 'good' joints, though heel fillets are poor. The solder pa
Electronics Forum | Fri May 29 08:25:13 EDT 2009 | floydf
We are getting what looks like cold solder joints on one of our boards. The boards have an aluminum substrate, and use OSP plating. The solder is lead free - 96.5 Sn, 3.0 Ag, .5 Cu. The flux is no clean. When we first had the problem, my solder profi
Electronics Forum | Wed Jan 11 22:47:31 EST 2006 | davef
We didn't intend to light anyone's fur on fire [get anyone's underwear in a knot, roil the waters, have a cow man] about consultants. The Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste
Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Fri Jul 30 16:02:49 EDT 1999 | Earl Moon
| | I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | | This ceramic su
Electronics Forum | Thu Jul 29 23:21:51 EDT 1999 | CH Lee
I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. This ceramic substrate