Electronics Forum | Thu Jul 20 13:08:35 EDT 2000 | Bob Willis
The solder paste formulation is different 63/37 is a tin lead alloy so t here is one difference from a lead free. Yes you can get no clean lead free products but if you compare the amount of visible residues they will be normally higher. So far most
Electronics Forum | Wed Oct 19 11:33:15 EDT 2011 | caerleon
easier if you recycled on-site? You can still send off for reclaimation the oxide powder that your left at the end of the process. Failing that talk to your supplier to see if they have arrangements to do this for you or look at reducing dross - i f
Electronics Forum | Sat Oct 18 09:30:43 EDT 2008 | hussman
Sounds like a part problem. You can SOMETIMES over come this with a hotter profile. We see this a lot with brokered parts. Seems like a lot of people are rejecting parts because a lot of companies haven't perfected their RoHS process, yet produce
Electronics Forum | Fri Jul 20 08:09:09 EDT 2007 | chrispy1963
In passives I dont know if anything changed at all other than the terminal plating. As for Active components there has been much engineering done to allow for the extra heat needed to liquify say SAC305 or other lead free pastes without damage to th
Electronics Forum | Wed Feb 21 14:14:11 EST 2007 | rgduval
Hi, Bill, Lead-free solder and paste manufacturers will be a great resource for you during the transition; they've tested their products extensively, and their application groups have been able to help me through the biggest changes. There are a fe
Electronics Forum | Wed Jan 07 15:48:22 EST 2015 | jacklucas
We switched our PCB's to 170Tg over 10 years ago, so we're probably good to go on the temperature aspect. Thanks for the opinion on the added lead content.
Electronics Forum | Tue Jan 06 16:31:41 EST 2015 | jacklucas
In switching to lead free processing, we find ourselves having over 400 PCB part numbers with Sn63 HASL finish. And there is no hope of quickly purging inventory and getting our drawings changed to call out a lead free finish. I want to avoid having
Electronics Forum | Tue Jan 13 04:35:26 EST 2004 | pablowe
We have done some trials with Lead free which appear to have gone well. We will be introducing a number of new products over the coming months and it is an opportune time to begin using lead free on these products which will be required by law in the
Electronics Forum | Thu Dec 22 12:05:37 EST 2005 | Tony
Currently we are using a 2 step vapor soldering process to manufacture our std. lead soldered parts. The first step was done with a ls240 vapor fluid and the second was done with a ls200 fluid. Using a 221 deg C sn95/Ag5 solder for the first step a
Electronics Forum | Tue Sep 28 19:54:22 EDT 2004 | KEN
If we are talking about Indium...then you will eventually be paying what everyone else is. The resource is diminishing especially with the application into the display markets. Same with silver. We are comming out of an all time low for silver....