Electronics Forum | Thu Jan 05 17:06:38 EST 2006 | russ
Is it now acceptable to discard the SAC alloy directly into the trash or is it still a requirement to dispose of through hazmat procedures. Seems to me that we can now just chuck the old paste right into the normal trash since it is the replacement
Electronics Forum | Wed Feb 16 12:34:49 EST 2005 | greg
Hi all We recently have a problem with component in package 0805 (capasitor 100nF). I have noticed that after reflow soldering only one lead of the component is soldered. The second one is just laying on the PCB land. We use screen printing process
Electronics Forum | Thu May 06 06:47:12 EDT 2004 | praveen
Hi, I just need to undestand any issue? If I mount Pb free BGA and use normal SN/Pb solder paste?
Electronics Forum | Wed Jun 02 19:01:50 EDT 2004 | lynnmc
Thanks to all on this feedback
Electronics Forum | Tue Jun 01 17:37:34 EDT 2004 | lynnmc
Any view on what the minimum reflow temperature is for a SAC ball bga to form a reliable joint with PbSn solder?
Electronics Forum | Wed May 24 15:59:34 EDT 2006 | JohnM
I have a product with mixed in Pb free and Pb BGAs. I decide to use SnPb paste with Pb free reflow profile to make it work for both types of BGA. Do I have a reliability solder joint issue by using this method? How is your opinion on this case? Can
Electronics Forum | Tue Jun 01 19:25:19 EDT 2004 | Ken
...oops part 2: I will assume a sac 350 ball??? 217-218C this will completely reflow the ball and form a "normalized" joint with a collapsed structure.
Electronics Forum | Thu Oct 30 21:55:27 EST 2003 | johnwnz
Now I've checked the archives on this and found the starts of an answer but not much else, but then that posting was a while ago and I though there would be some more data now. So here's the question: who, if anyone is placeign Pb-free BGA's (ideally
Electronics Forum | Thu May 06 08:59:25 EDT 2004 | davef
Even with PbSn solderpaste the leadfree BGA's have a superior resistance to solder-joint fatigue failure when compared to conventional parts. [Solder Fatigue Reliability Issues in Lead Free BGA Packages, Pedro Chalco of IBM, Pan Pacific Microelectron
Electronics Forum | Tue Jun 01 19:23:15 EDT 2004 | Ken
profile it for the tin/lead paste. The tin in the solder paste will begin to disolve the sac ball. This is exactly the same scenario as 90/10 (80/20)high temp balls found on ceramic bga and many super bga devices (except the sac balls are now tin r