Electronics Forum | Wed Oct 18 07:51:14 EDT 2006 | davef
Look here: http://www.circuittechctr.com/ As a low cost approach, use copper foil purchased from a stained glass window hobbyist shop. Cut foil pieces to size with a sharp knife. Epoxy the pieces in place of the damaged pads. Tin and then solder th
Electronics Forum | Sun Feb 22 15:46:09 EST 2015 | slave2anubis
Hi, my name is Dacian, and i run a mobile phone repair shop in Timisoara, Romania. Lately we decided to do more advance motherboard repair jobs, and a big problem that we have is, cleaning the board after we remove the chips. We repair manly iPhone,
Electronics Forum | Fri Aug 07 01:02:51 EDT 1998 | zeek - just wanna to get a word in here
| | I am looking for advice or information from anyone about the possible reliability problems associated with epoxy on solder pads of discrete devices. Will the epoxy expand and lift over time, Will there be adverse reaction between the solder and t
Electronics Forum | Fri Apr 03 08:26:58 EST 1998 | Scott Cook
| I am looking for a product to repair PCB mask (seal exposed copper) and fill Gouges in pcbs, any suggestions? Why not use an electonic grade 5 minute epoxy? As long as it's inert, I'd do it. Scott
Electronics Forum | Sat Apr 04 15:28:36 EST 1998 | Use one of our UV cure conformal coatings
| | | I am looking for a product to repair PCB mask (seal exposed copper) and fill Gouges in pcbs, any suggestions? | Why not use an electonic grade 5 minute epoxy? | As long as it's inert, I'd do it. | Scott
Electronics Forum | Thu Oct 05 17:05:36 EDT 2000 | JAX
These types of foil kits work just fine as long as they are used before expiration. Scraping off the epoxy coat gets a little tough on fine pitch pads and etches. I have always like to use a solder sample board to retrieve my bits & pieces from whene
Electronics Forum | Wed Aug 09 19:14:15 EDT 2006 | Board House
Our Manufacturing policy regarding welds is as follows. 1) Inner layers - depends on Core thickness and line width. Our shop will not do any welding on core thickness less then 5 mils. or line width less then 5 mil. Good AOI practices reduce the a
Electronics Forum | Thu Jun 02 11:16:23 EDT 2005 | JH
I concern about the Through Hole soldering as well. Currently, we have encountered some problems of Multilayer from Through Hole soldering. The root-cause is probably related to PCB Finish, machine setting, Thermal relief Pad or hole and something e
Electronics Forum | Sat Aug 07 11:10:03 EDT 1999 | JohnW
| Could someone give recommendation on the stencil opening for printing epoxy on HAL FR4 PCB for 0805 and 0603 size chips capacitors and resisitors. | My regular stencil manufacturer recommend the following: | Thickness: 8 mils | 0805 opening: Oblong
Electronics Forum | Thu Aug 25 01:30:47 EDT 2016 | souldierann
Hi folks, I hope you can help me on how to repair broken pcb pads.
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830