Electronics Forum | Mon Jan 26 07:27:43 EST 2004 | loz
I have a product that has earthing/positioning holes, as they are to be used for earthing purposes they need to be free from conformal coating. This pcb is double sided. I have used spot/peelable mask to protect these holes. However when the conforma
Electronics Forum | Thu Jul 01 14:47:10 EDT 1999 | Tony
| | | My guess would be trapped flux continuing to be active after soldering. Is the tarnish there immediately after exiting the machine? Do you remove the mask and wash right away? If the solder is reflowing under the mask on the component side
Electronics Forum | Wed May 03 15:00:44 EDT 2006 | patrickbruneel
It all depends on process, design and environment in which the contacts are used. Both have excellent conductivity characteristics Both don't oxidize over time On the other hand gold is much softer then carbon, and after hitting that contact a gazil
Electronics Forum | Fri Apr 07 17:17:55 EDT 2000 | Dave F
Ashok: You should select and use low residue tapes. But ya know, ya go out and research a great tape and if yer not careful, the buyer will second source ya and (surprise) ya got residues again. We have found that Lemme say this about Katon tape
Electronics Forum | Mon Sep 27 08:52:11 EDT 1999 | Brian
| i had a problem here, during the wave soldering process, we apply a water soluble mask on the gold finger to protect it from contamination. But after washing, there is still some mask left on the gold finger. | Can anyone pls advise is there any pa