Electronics Forum | Thu Jul 24 10:49:12 EDT 2008 | slthomas
100 CFM at each exhaust if you're using room air, 25 CFM/ea if you're using nitrogen (according to my manual...never used nitrogen myself) per their specified delivery rates.
Electronics Forum | Thu Sep 23 16:14:39 EDT 2004 | russ
Control the temp during removal and re-use them. Do not exceed reflow parameters during removal. They should be good up to around 5 reworks. My opinion Russ
Electronics Forum | Fri Mar 27 19:24:25 EST 1998 | Frank Fan
| Where I can buy the used Fuji or panasonic SMT line?
Electronics Forum | Mon Mar 16 15:57:05 EST 1998 | J. Hughes
| Where I can buy the used Fuji or panasonic SMT line?
Electronics Forum | Thu Mar 21 11:19:42 EST 2002 | bmulcahy
Why not go back to your suppliers and see if they will take the reels for re-use ?
Electronics Forum | Thu Jul 26 22:56:03 EDT 2007 | davef
And they're using a stencil that is how thick?
Electronics Forum | Fri Oct 07 01:45:21 EDT 2011 | thmeier
We´re using Viscom
Electronics Forum | Mon Feb 28 09:33:29 EST 2005 | lyrtech
Actually we're using ALPHA METAL Vaculoy 63SN/37Pb solder bars in our WAVE (ELECTROVERT ULTRAPACK 650C). With that solder, we use the ALPHA METAL LONCO SLS 65C flux. With this combination, we have many bridges and sometimes, the solder do not full co
Electronics Forum | Thu Mar 12 13:26:16 EDT 2009 | rgduval
We're using Sn100C at wave. Well, to be fair, in a static solder pot; as we don't have a lead-free wave machine in operation at the moment. We've had generally good experiences with the SN100. Good soldering; some blow holes, but, since we're usin
Electronics Forum | Tue Sep 15 06:16:35 EDT 2009 | geb
Hi, We're using solder paste opposed to solder wire for hand soldering certain components. We are also using high temperature soldering irons with 450deg C tips as we are soldering onto aluminium (IMS) PCBs. The quantity of tips which we go through