Electronics Forum | Fri Apr 17 14:08:00 EDT 2015 | davef
Humiseal says, "UV cure – These materials are also more difficult to repair as they are the most chemically resistant and mechanically tough of all conformal coatings. Removal is possible locally by using powder abrasion."
Electronics Forum | Fri Apr 17 08:52:03 EDT 2015 | charliedci
Thanks for the info Sarason. The UVCL is a Urethane. Did not want that hard of finish (for solder rework issues). We like the Acrylic as acetone will remove cured material for solder rework.
Electronics Forum | Mon Aug 09 07:13:08 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problemsd
Electronics Forum | Tue Aug 10 01:02:31 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problems
Electronics Forum | Fri Jan 22 10:17:47 EST 1999 | LeeAnne
I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the coa
Electronics Forum | Wed Jul 02 02:46:44 EDT 2008 | tang
Hi Guys, I have few question would like to ask regarding pcb conformal coating: 1. Can I know which masking material is the best for easy apply, fast cure, fast & easy to remove after coating & baking. And no chemical reaction which will whiten the
Electronics Forum | Mon Dec 27 10:03:35 EST 2010 | duso02
Contact your distributor for the coating or Humiseal directly. Humiseal has had a recent issue with batches of 1B31. The specific problem is lack of adhesion, which is what you have as well. You need to find out if your batch # is one of the affected
Electronics Forum | Mon Jan 03 00:30:30 EST 2011 | raghu
Contact your distributor for the coating or > Humiseal directly. Humiseal has had a recent > issue with batches of 1B31. The specific problem > is lack of adhesion, which is what you have as > well. You need to find out if your batch # is one >
Electronics Forum | Sun Dec 26 23:48:01 EST 2010 | raghu
Dear Sir, We are using 1B31 conformal caoting of 48 sec viscosity in Zahn #1 cup, by machine(PVA354) application with Tank air pressure 2.3 psi, automising air pressure 1 psi. 7 days after application we are observing peeling off problem.. And n
Electronics Forum | Mon Oct 14 15:13:52 EDT 2013 | esoderberg
Does anyone have a novel idea on how to protect the flex area during conformal spray coating? Currently using Humiseal T30 on the flex but it has to be removed very carefully to insure coating stays intact on the board.