Electronics Forum | Tue Jan 14 07:33:16 EST 2014 | leardkattiya
Hi I have solder paste that suppose to be stored to 0 - 10 degree celsius. However due to broken fridge, we decided to stored on -40 degree celsius freezer. Does the solder paste still good to be use? Please help.
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Tue Jun 26 19:59:08 EDT 2001 | davef
They always tell you to calculate ROI, when they want to blow you off. Do a net search using - calculate ROI. Links to three pretty good descriptions on this are: http://www.dmreview.com/editorial/dmreview/print_action.cfm?EdID=2487 http://www.eval
Electronics Forum | Wed Mar 14 18:29:04 EST 2001 | mparker
The basic rule of thumb (info current as of 9/2000, from Ceeris and others) is the 10X multiplier for each major process step. Catching a defect and correcting in SMT will cost $0.10 each. (think about $.04 placement cost, stop line time, operator h
Electronics Forum | Wed Sep 26 14:58:46 EDT 2001 | bobm
i have stored boards in the refrigerator in side a tray (with a lid) for 2 days and still had them reflow with no problems. i don't know if i would go any longer than that. i would not put any qfp's or any other device that is moisture sensative dev
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 15:10:14 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon Sep 03 08:56:26 EDT 2001 | henriksn
Hi everyone, I work in a development firm, that has a small prototype department. We have recently invested in a small automatic SMD pick&place machine. When mounting over 100 different components, the machine runs out of feedercapacity, and the res