Electronics Forum | Fri Jan 26 13:26:30 EST 2007 | rw
We are developing a new product that requires conformal coating on the motor controller. We selected a silicone based conformal coat due to its ease of use. There has been disagreement among engineers as to its impact on the motor. We have contact
Electronics Forum | Thu Feb 01 08:47:07 EST 2007 | davef
NASA is concerned about outgassing in high-vacuum environments. They select materials to minimize outgassing. http://outgassing.nasa.gov/og_desc.html
Electronics Forum | Wed Apr 19 11:50:05 EDT 2006 | amol_kane
Hi BJ, Everyone's favourite answer...it depends! If the volume if large, masking boots will save you both, time and money in the long run. Custom boots are relatively expensive to buy, but they pay themselves over time by savings on masking tape. ma
Electronics Forum | Thu Aug 27 11:35:07 EDT 2009 | davef
There are many possibilities: * Conformal coat is incompatible with surface residue on the board * Conformal coat is incompatible with solder mask on the board * Moisture is out-gassing from the board * Conformal coat is too thick and does not allow
Electronics Forum | Thu Aug 27 08:34:50 EDT 2009 | floydf
I am having trouble with little air bubbles in my conformal coat. It ranges from a few pin sized bubble to looking like spit. We are using Dow 2620 silicone conformal coat applied with a PVA sprayer machine. The conformal coat comes in bladder bags t
Electronics Forum | Fri Oct 09 16:07:30 EDT 2009 | dlabelle
We use Dow 2620 silicone conformal coat applied with PVA1000 sprayer machine. If used on a daily bases, we have no problem. If we let the machine sit idle for over a week, we will get bubbles in the conformal coating. Sometimes, purging the line w
Electronics Forum | Mon Jan 28 11:50:23 EST 2013 | johng
Good morning Mark, No issues around the masking at this point. The issue seem to be in open areas as well as between clad runs. We are using Humiseal 1A33 Conformal Coat.
Electronics Forum | Fri Jan 25 12:23:07 EST 2013 | dontfeedphils
By "they've been through the wash cycle twice" what do you mean? What kind of cleaning process do you use? What sort of chemistry? How do you handle the assemblies after wash and before coating? Do the operators where power free gloves? -Phil
Electronics Forum | Fri Jan 25 12:14:18 EST 2013 | johng
I'm using urethane conformal coat and have fisheyes and dewetting after coating even though the PWAs have been through the wash cycle twice. I'm looking at using Ionox 13302 in an ultrasonic cleaner as a short term solution until root cause can be id
Electronics Forum | Fri Jan 25 12:15:04 EST 2013 | johng
I'm using urethane conformal coat and have fisheyes and dewetting after coating even though the PWAs have been through the wash cycle twice. I'm looking at using Ionox 13302 in an ultrasonic cleaner as a short term solution until root cause can be id