Electronics Forum | Mon May 14 17:16:27 EDT 2001 | slthomas
We use both, cartridges for water soluble and jars for no clean. The only reason we do is so they can't possibly (knocking on my head) mix it up. Pros: Jar - you can put paste back into it if you want to wash your stencil, change jobs after lunch,
Electronics Forum | Tue Jul 16 12:24:25 EDT 2019 | slthomas
In VERY general terms, water soluble flux is usually better at getting good wetting of the soldered connections unless you have a very well controlled process, in which case no-clean can be very handy (you don't have to clean). Water soluble flux re
Electronics Forum | Wed Mar 10 09:52:22 EST 1999 | justin medernach
| We are starting up an SMT line with a printer and convection oven.... The area we are considering for the printer is totally uncontrolled for humidity, temperature and even cleanliness. | | We are working on the filters to keep particulates down,
Electronics Forum | Mon Jan 19 20:25:52 EST 1998 | Steve Gregory
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Mon Nov 01 16:22:47 EDT 2010 | jax
Who Cares... Mix Away! Although you should not mix different Solder Pastes' together in a container or on a stencil (Mostly due to the flux, although solder sphere size and shape could cause an issue), mixing solder brands or chemistries on a board
Electronics Forum | Tue Feb 19 19:36:21 EST 2002 | davef
You weren�t clear but I assume the problem is not widely distributed and affects only a few parts on each board. Do this trick: * Cut a ~1� piece of fairly serious wire, like 18 or 12 AWG. * Strip the insulation. * Gear-up with gloves, glasses, and
Electronics Forum | Tue Aug 14 17:55:01 EDT 2001 | Boysen
Are you using a water soluble paste? Older generations of water soluble paste are notorious for voiding. Some of the new generation water soluble fluxes allow a much wider process window.
Electronics Forum | Wed Sep 26 12:16:44 EDT 2012 | bwjm
Hi Guys,recently i am facing an issue. Refer to the attached photo. This PCB is high RF speed, gold immersion single layer. After reflow, my solder seems to have black stains on it. I tried with SAC305 paste water soluble and no-clean, both results a
Electronics Forum | Tue Jun 26 19:51:31 EDT 2001 | davef
Rosin. A hard, natural resin, consisting of abietic acid [and pimaric acids in Europe] and their isomers, some fatty acids, and terepene hydrocarbons. Rosin is extracted from pine tree stumps. It�s an organic material distilled from oleoresin in p
Electronics Forum | Thu Aug 24 15:37:50 EDT 2006 | Chunks
Hi Any, This is from an earlies thread "Solder Ball After Reflow Process". Date: August 16, 2006 01:52 PM Author: Russ Subject: Solder Ball After Reflow Process Oven settings are meaningless here. What does the board see? It is the paste we a