Electronics Forum | Mon Feb 20 09:20:07 EST 2006 | dpmilk
It appears to us that the problem lies in the lead-free solder paste rather than the inductors. We have not found a lead-free solder that does not do this. The green is on the copper wire. We believe it gets there during the reflow. The gasses fr
Electronics Forum | Mon Oct 08 21:05:00 EDT 2001 | ksfacinelli
DO NOT Mix Technologies.... If you are using a no clean solder paste use a no clean wave solder process. I have direct experience with using a no clean paste and a RA water-soluble wave solder process. When cleaning with the water wash system your
Electronics Forum | Wed Nov 22 10:28:33 EST 2000 | Victor salazar
We have some humidity issues due to monsoon season in southern Arizona, I am having issues with water soluble solder paste, and moisture sensative IC's. We are trying to maintain a 32% relative humidity for EESD purposes. What is the standard, and w
Electronics Forum | Fri Dec 10 08:32:30 EST 1999 | Larry
Ron, Kester also makes another water soluble paste (#R598) that works great on these parts! Down side is the tack life is a little shorter
Electronics Forum | Sat Jun 26 14:15:28 EDT 2004 | PCA
Does any one have the best recommendation for a water soluble solder paste for use with fine pitch parts and micro BGA's and immersion gold pads.
Electronics Forum | Fri Nov 19 10:14:30 EST 2004 | steve
A customer of mine is having problem. They can't control their humidity. It is very dry. RH averages 28-30%. The water soluble solder paste prints great. But dries out on metal squeegee. Any suggestions.
Electronics Forum | Fri Aug 04 09:09:22 EDT 2006 | russ
Aj is right, utilize the homeplate aperture, this reduces the amount of paste actually underneath the component, Pb frees exhibit this mid ship more often than the lead, I think,it is mostly because of thre transition to noclean form water solubles
Electronics Forum | Sat Jun 11 07:24:26 EDT 2005 | buchi79
Russ, Thanks.By the way, i already look into the reflow profile & paste storage & thowing requirement. Even i cut down the stencil life to 4 hr to avoid any moisture absorbtion. If i were to change the paste formulation, what would you propose ? But
Electronics Forum | Sun Apr 18 07:01:10 EDT 2004 | Nick Prince
"Thanks for all your informative replies. I do know that Motorola is using a No Clean Eutectic Solder for their BGA's. We are in Aerospace and is using a Water Soluble Paste Flux." This statement is confusing me (not to difficult at my time of life)
Electronics Forum | Thu Mar 30 07:10:56 EDT 2017 | nickywan
I have a problem with some particle, dust and solder paste contaminate on PCB rack and need to clean up once a week by manual. Now looking for the equipment to do Inline cleaning with water jet & Hot air Dry concept. Not too big machine and concept l