Electronics Forum | Thu Aug 12 20:32:44 EDT 2004 | usdigital
Indy, We use Palladium silver surface finish parts for silver epoxy attached parts only. It is our understanding that this finish is not for solder, but only silver epoxy attach. I expect that is you problem. Dave
Electronics Forum | Sun Jul 04 19:49:05 EDT 2004 | indy
Hello Everyone, We are having some problem with Palladium-Silver surface finish. We have ceramic components with the above surface finish. When we try to assemble these on Sn/Pb solder, we are observing open joints. If we reflow the compt for more t
Electronics Forum | Thu Aug 12 18:06:09 EDT 2004 | SR
May I ask what component types you are using and who the suppliers are? FYI - If the components have exceeded their shelf life, they may have oxidized too much for soldering using low activity fluxes. Thanks and best regards, SR
Electronics Forum | Tue Jul 13 16:35:25 EDT 2004 | Richard
Sounds like your Si plalladium finish has oxide on it from the firing or sitting around too long. I used to assemble LTCC and have had plenty of dealings with this matter. The best and easiest is to get an active type flux and solder paste. AIM makes
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Mon Feb 18 03:40:04 EST 2008 | akareti
Hi everybody, I found a defect varistor 0603 Tombstone and poor welting when we use component that terminal is Silver palladium (Ag/ Pd) with Leaded solder paste (63/37). Then we change alternative component that terminal is Ni/ Sn the result not fou
Electronics Forum | Thu Apr 29 22:50:41 EDT 1999 | Kelly Morris
Tombstoning 0805s w/palladium/platinum/silver terminations We are experiencing tombstoning problems on 0805 packages that have paladium/platinum/silver terminations. It comes & goes...... I�ve checked the reflow profile, and paste deposition and a
Electronics Forum | Mon Mar 30 08:11:22 EST 1998 | Derek Drabenstadt
Does anyone have any experience with fired-silver/platinum/palladium lead terminations soldering. I have had issues on nickel over gold plated boards but not with HASL'd boards with tin/lead pads. Is this the norm?
Electronics Forum | Tue Jul 06 00:13:13 EDT 2004 | indy
john, Immerson Silver is probably a good choice. What is your opinion abt Palladium silver. Does presence of Palladium affect the reliability of the pcb surface finish