Electronics Forum | Tue Mar 20 06:09:20 EDT 2007 | d0min0
Hi, can't find answer to my question on web - maybe someone can help would it be compatible to use a wire of Sn62Pb36Ag2 for a product made with Sn63Pb37 paste ??? regards
Electronics Forum | Wed Aug 06 14:49:06 EDT 2014 | dyoungquist
Sn62Pb36Ag2 has a higher liquidus point of 189C as compared to Sn63Pb37 at 183C. You may need to slightly adjust your oven profiles to use it compared to SnPb. We have had good solder-ability and reliability with it in our IPC Class II products. A
Electronics Forum | Sat Aug 30 12:36:05 EDT 2008 | omid_juve
we are doing many experiment on this problem 1)sn63 pb37 solder paste +normal profile 2)sn62 pb36 ag2 solder paste +normal profile 3)pb free solder paste + pb free profile 4)sn63 pb37 solder paste + pb free profile but still the problem exist so i th
Electronics Forum | Thu Apr 15 09:45:34 EDT 1999 | Terry Keen
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Apr 13 08:08:33 EDT 1999 | Rob Palson
We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to bu
Electronics Forum | Mon Apr 19 02:38:41 EDT 1999 | Brian Sloth Bentzen
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Sun Apr 24 09:12:00 EDT 2005 | davef
We're not sure what your customer is talking about either. Gold and tin form an intermetallic compound [IMC] that can cause poor solder connections. To minimize the potential of a problem, keep gold to less than 3 percent of the metal. [Search the
Electronics Forum | Tue Nov 21 09:46:19 EST 2006 | jax
I assume you are talking about Sn62Pb36Ag2 solder. You should not see any added concerns when subjecting Sn62 to multiple reflow cycles as compared to Sn63. As compared to Sn63Pb37: Reduced leaching issues Increased Wetting due to lo
Electronics Forum | Thu Apr 15 08:21:47 EDT 1999 | Terry Keen
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Tue Apr 13 09:11:54 EDT 1999 | Dave F
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
.gif)