Electronics Forum | Fri Dec 13 12:12:21 EST 2002 | Hank Sybesma
We are being asked to begin rework processes on boards that use lead free solder. Does anyone have any experience in the service field working with lead free?
Electronics Forum | Thu Oct 01 09:58:30 EDT 1998 | Jacqueline Coia
Could you tell me please when the lead free solder regulation will become mandatory in Europe and also what are the current industrial alternatives for paste, bar and wire. Cheers, Jack
Electronics Forum | Wed Feb 20 23:17:34 EST 2002 | surachai
I AM JUST EVALUATION LEAD FREE EVALUATION AND FOUND THE BIG PROBLEM OF SOLDER CRACK BETWEEN TERMINAL OF COMPONENT AND THE INTERMETALLIC LAYER OF LEAD FREE ALLOY BUT DON'T FIND ANY CRACK BETWEEN SOLDER AND SURFACE OF PCB , COULD YOU HELP ME VERIFY T
Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Wed Oct 07 15:44:43 EDT 1998 | CW
There's a good article on lead-free assembly of mixed technology in the May issue of SMT Magazine (pg. 52)
Electronics Forum | Fri Dec 13 16:39:42 EST 2002 | Gris
Hi, Look for papers on SMTA there are a lot of papers on lead free rework. If you dont find any let us know here I am sure you will receive many. Here are a just a few http://www.google.com/search?hl=en&ie=UTF-8&oe=UTF-8&q=%22lead+free+rework%22&
Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS
It may be you should look for higher TG of Durapol Rgds GS
Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram
Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle
Electronics Forum | Tue Jun 03 18:34:22 EDT 2003 | Kris
Hi, There have been other studies where it was found that lead-free soloder joints are more reliable than tin-lead solder joints irrespective of test conditions. In fact the automotive industry has been using Sn/Ag for underhood applications for a
Electronics Forum | Thu May 29 18:58:41 EDT 2003 | davef
Lead free solder is bad for the environment, while increasing product costs. The US looked at restricting lead use a few years ago, took no action, and has no plans to enact frivolous legislation like the "greens" have foisted upon the Eurolanders a
winsouce.jpg)