Electronics Forum | Thu Jun 26 21:38:31 EDT 2003 | Dreamsniper
Hi Guys, Need your good advice about this for a 5 thou stencil thickness: 0603 pad is 50mil x 40mil 0805 pad is 75mil x 45mil 1206 pad is 70mil x 50mil I want the above apertures to be in IPC STD Homeplate Design + an area reduction of 15%. Will t
Electronics Forum | Wed Jun 24 16:45:18 EDT 1998 | Bill Schreiber
| I know this topic has probably been talked about before...But I ran into a small situation where Solder Balls were appearing in large quantities on the PCB....the Problem has been isolated and taken care of, my question is, what are some good metho
Electronics Forum | Sun May 30 08:50:42 EDT 1999 | Dave F
| Yes l know this problem keeps cropping up on the forum but l've missed some of the follow-ups. | | Our problem is that the lifting only occurs on 3% of production so actually detecting an improvement is difficult. We're actually having to inspect
Electronics Forum | Sat Jun 30 11:03:29 EDT 2001 | davef
Nice to have you back on SMTnet. Some of the newer folk have missed-out on the solid contributions you�ve made to the Forum. The chicken wire cleaning basket was a classic!!! [It�s a shame that the folk at SMTnet can�t recover those files.] We bu
Electronics Forum | Thu Sep 26 11:44:23 EDT 2002 | abelardo
Hello everyone out there in the SMT world. I have a dilema I'm currently running a board that has 3 csp's with a .75 mm. ball pitch and .3mm ball size. And 2 qfp's-160. The stencil is 4 mils thick and I'm using a 63/37 solder paste. My reflow prof
Electronics Forum | Thu Jun 17 10:20:15 EDT 1999 | Brian Wycoff
| | | Dear All, | | | | | | We are having a big debate over what is the industry standard in DPPM on the wave sodlering process. is a DPPM of about 800 satisfactory. As per our big bosses it should not be more than 50 DPPM. Is the figure realistic
Electronics Forum | Tue Jul 31 18:49:20 EDT 2001 | arsmoriendi
i have a problem with some units that had one capacitor only soldered in one side, the geometry of the capacitor is 0805, our product during his life suffer a lot of stress (due temperature or vibration), some of those units are already with the cost
Electronics Forum | Tue Mar 07 14:18:32 EST 2006 | James
Billy, I have to disagree with you. We inadvertently soldered a Pb BGA with SAC305 paste and then had it micro sectioned and spectrum analyzed. Imagine our surprise when we saw the spectrum analysis showed Pb. The micro sections showed none to ac
Electronics Forum | Fri Mar 23 15:33:53 EDT 2007 | ppcbs
Does anyone know where to purchase 90/10 & Lead Free solder balls and kits for BGA Reballing? I'm having service problems with my current vendor who decided that they no longer wish to sell 90/10 balls, can't take in an order without a quote, and ca
Electronics Forum | Thu Jun 24 10:48:02 EDT 1999 | Earl Moon
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel