Electronics Forum | Thu Oct 01 09:58:30 EDT 1998 | Jacqueline Coia
Could you tell me please when the lead free solder regulation will become mandatory in Europe and also what are the current industrial alternatives for paste, bar and wire. Cheers, Jack
Electronics Forum | Wed Jul 13 15:14:17 EDT 2005 | jdumont
Oh you mean like the no heat soldering irons? I think they can also cook you a pizza while soldering wires.
Electronics Forum | Sun Sep 23 18:59:59 EDT 2007 | darby
I presume you are looking at low melting point solders. Firstly, I would consider running BOTH sides with the same paste - this will cut down the opportunities for a mix up with rework or retro-fit. Secondly, check that there is a cored wire availabl
Electronics Forum | Tue May 13 07:04:54 EDT 2014 | hemant_pang23
I am looking for the solder wire leaded or lead free which can withstand the solder joint at temperature 450deree Celsius or more after soldering, since i need to form a solder joint at higher temperature area Pls suggest the part number for the sam
Electronics Forum | Thu Dec 21 21:37:19 EST 2006 | Jack
Hi Pavel, Real Chunks, Thanks for your valuable inputs..Selecting the correct location for board profiling is critical in determining the solder joint quality. Am I right to say TC wire attachment locations priority should be as below: (1) Thermal
Electronics Forum | Tue Feb 28 08:08:06 EST 2006 | davef
Tin is an excellent solvent. So, whether using lead-free or leaded solder, your wire will neck to one degree or another if the material of the wire dissolves in the metal of the solder.
Electronics Forum | Wed Jan 21 12:25:45 EST 2015 | dyoungquist
Kester makes a thermocouple solder: Alloy SN10PB88AG2 Flux "44" Core 58 Diam 0.031" I have used this to solder thermocouples to pcbs when profiling for lead-free temperatures. When done you can unsolder the thermocouple and reuse it again. This g
Electronics Forum | Thu Apr 15 10:58:16 EDT 2004 | mwg9184
I am trying to put a center support on a wave solder machine for lead free soldering. My problem is that every metal I use is interacting with the lead-free metals and thus eating away the center support. I have tried titanium, stainless steel. I am
Electronics Forum | Fri Oct 06 04:23:06 EDT 2006 | David
What is the solder finish of the board?. If this is gold, maybe you should check the reflow profile and max temperature which can easely kill your gold coating so problems with bonding. Also we are using Prozone Multicore with ultrasonic to clean
Electronics Forum | Wed Feb 16 17:28:14 EST 2005 | davef
Greg: As we understand it, in your situation: * One 0805 lead solders to board properly * Another 0805 lead does not solder On the 0805 lead does not solder, there does the solder go? * On the pad * On the component lead A common solderability test